1) gunning material
喷补料
1.
The effect of the Fe2O3 content in gunning material on the ability to resist CO damage,and the reaction mechanism of the carbon disposition in refractories are analyzed.
以自行开发的适用于高炉中上部使用的喷补料为基料,通过添加Fe2O3粉改变料中的Fe2O3含量,研究了Fe2O3含量对高炉喷补料抗CO破坏能力的影响,初步分析了产生破坏作用的机理。
2.
The resisting ability of gunning material for blast furnace to CO corrosion was invesitigated under the pure CO and the mixed gas condition through adding hydrogen into pure CO.
通过在反应气中加入氢气，研究此种气体组成条件下，喷补料抗CO侵蚀能力。
3.
This paper described the effect of Fe2O3 content in gunning material for blast furnace on its resistance to CO.
研究了高炉喷补料中Ｆｅ_２Ｏ_３的含量对其抗ＣＯ侵蚀的影响，研究表明，随喷补料中Ｆｅ_２Ｏ_３含量增加，其抗ＣＯ侵蚀能力急剧降低，因此减少喷补料中Ｆｅ_２Ｏ_３的含量有利于提高其抗ＣＯ侵蚀能力，延长炉衬寿命。
2) Gunning Refractory
喷补料
1.
Thermal Shock Resistance of Gunning Refractory Composed of Aluminium Silicate;
硅酸铝质喷补料热震稳定性研究
2.
Gunning refractory are made and its properties,such as linear change during baking and thermal shock resistance, are measured.
配制系列高炉喷补料，并检测其烧后线变化及耐热震性等性能。
3) Gunning mix for BF
高炉喷补料
4) Composition of gunning refractory
喷补料组成
5) gunning mixture particles
喷补料颗粒
6) magnesite meding material
镁质喷补料
补充资料：喷补料
分子式：
CAS号：
性质：由具有一定颗粒级配的耐火集料、化学结合剂和外加剂组成的，用喷射施工方法对热工设备内衬进行修补时使用的不定形耐火材料。是喷射料中一种主要类型。按喷补用材料状态和喷射方法可分为三种：（1）湿法喷补，一般只能进行薄层修补。（2）干法喷补（也称为半干法喷补），可进行较厚层喷修，使用最为广泛。（3）火焰喷补，可获得结构致密的喷补层，结合强度高，抗侵蚀性的抗冲刷性强。喷补料的粒度组成和极限粒度应根据喷补机的结构、喷补层厚度以及不同的喷补方法来确定。粒度选择不当或颗粒级配不合理，对喷补料的附着性和喷补层的密度有很大影响。
CAS号：
性质：由具有一定颗粒级配的耐火集料、化学结合剂和外加剂组成的，用喷射施工方法对热工设备内衬进行修补时使用的不定形耐火材料。是喷射料中一种主要类型。按喷补用材料状态和喷射方法可分为三种：（1）湿法喷补，一般只能进行薄层修补。（2）干法喷补（也称为半干法喷补），可进行较厚层喷修，使用最为广泛。（3）火焰喷补，可获得结构致密的喷补层，结合强度高，抗侵蚀性的抗冲刷性强。喷补料的粒度组成和极限粒度应根据喷补机的结构、喷补层厚度以及不同的喷补方法来确定。粒度选择不当或颗粒级配不合理，对喷补料的附着性和喷补层的密度有很大影响。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。