1) corrosion coupon
腐蚀试片
3) coupon corrosion test
挂片腐蚀试验
5) silver corrosion
银片腐蚀
1.
Analysis on silver corrosion in hydrogenated aviation fuel process;
加氢喷气燃料银片腐蚀不合格原因分析及对策
2.
The study has been carried out aiming at the unqualified silver corrosion of jet fuel in the oil truck and the result shows that it was caused by the element sulfur in oil truck.
针对喷气燃料装入罐车后银片腐蚀不合格的问题开展研究,结果表明主要为罐车含有元素硫所致。
3.
By studying the reation of carbon disulfide and silvor corrosion,author detected that only when carbon disulfide content excesscd 1%,it would lead the silver corrosion of the jet fuel.
通过对 33号添加剂加入量与银片腐蚀的关系的研究发现 :在喷气燃料中 33号添加剂的含量要超过 1%才会在短期内引起喷气燃料银片腐蚀不合格 。
6) silver strip corrosion
银片腐蚀
1.
The 3 # jet fuel produced by the diesel hydrotreating unit of Jiujiang Petrochemical Company was disqualified because of the silver strip corrosion test.
对九江分公司柴油加氢精制装置在切换生产3号喷气燃料时银片腐蚀不合格的问题进行了研究。
2.
Active sulphur and microbions may cause unquanlified results for silver strip corrosion test of jet fuel,which were then analysed and discussed especially from where they came.
分析了喷气燃料中导致银片腐蚀的两种物质活性硫和微生物,讨论了它们的来源。
3.
It is determined by analysis that the main factor affecting silver strip corrosion in aviation kerosene is element sulfur in active sulfide.
通过分析确定,影响航煤银片腐蚀的主要物质是活性硫化物中的元素硫,其含量达2 μg/g时就会造成航煤银片腐蚀不合格,硫醇和二硫化物等与元素硫共存时可促进银片腐蚀。