1) corrosion coupons
腐蚀挂片
2) carbon steel coupons
碳钢测腐蚀挂片
3) coupon corrosion test
挂片腐蚀试验
4) silver corrosion
银片腐蚀
1.
Analysis on silver corrosion in hydrogenated aviation fuel process;
加氢喷气燃料银片腐蚀不合格原因分析及对策
2.
The study has been carried out aiming at the unqualified silver corrosion of jet fuel in the oil truck and the result shows that it was caused by the element sulfur in oil truck.
针对喷气燃料装入罐车后银片腐蚀不合格的问题开展研究,结果表明主要为罐车含有元素硫所致。
3.
By studying the reation of carbon disulfide and silvor corrosion,author detected that only when carbon disulfide content excesscd 1%,it would lead the silver corrosion of the jet fuel.
通过对 33号添加剂加入量与银片腐蚀的关系的研究发现 :在喷气燃料中 33号添加剂的含量要超过 1%才会在短期内引起喷气燃料银片腐蚀不合格 。
5) corrosion coupon
腐蚀试片
6) silver strip corrosion
银片腐蚀
1.
The 3 # jet fuel produced by the diesel hydrotreating unit of Jiujiang Petrochemical Company was disqualified because of the silver strip corrosion test.
对九江分公司柴油加氢精制装置在切换生产3号喷气燃料时银片腐蚀不合格的问题进行了研究。
2.
Active sulphur and microbions may cause unquanlified results for silver strip corrosion test of jet fuel,which were then analysed and discussed especially from where they came.
分析了喷气燃料中导致银片腐蚀的两种物质活性硫和微生物,讨论了它们的来源。
3.
It is determined by analysis that the main factor affecting silver strip corrosion in aviation kerosene is element sulfur in active sulfide.
通过分析确定,影响航煤银片腐蚀的主要物质是活性硫化物中的元素硫,其含量达2 μg/g时就会造成航煤银片腐蚀不合格,硫醇和二硫化物等与元素硫共存时可促进银片腐蚀。
补充资料：腐蚀挂片
分子式：
CAS号：
性质：悬挂于测试容器内或现场盐测换热器或测试管道上，测定腐蚀用的标准金属试片。用以监测或评价冷却水系统的腐蚀状况。一般将预先处理和称重后的金属试片置入测试系统一段时间(如30～90天)，然后取出观察腐蚀情况，清洗称重，确定金属腐蚀失重程度(以密耳/年计，1mpy=0.0254mm/a)、腐蚀的类型以及点蚀深度等。金属挂片的数据除受腐蚀介质影响外，还与挂片表面处理、放置部位、暴露时间长短以及样片冶金方式等因素有关。
CAS号：
性质：悬挂于测试容器内或现场盐测换热器或测试管道上，测定腐蚀用的标准金属试片。用以监测或评价冷却水系统的腐蚀状况。一般将预先处理和称重后的金属试片置入测试系统一段时间(如30～90天)，然后取出观察腐蚀情况，清洗称重，确定金属腐蚀失重程度(以密耳/年计，1mpy=0.0254mm/a)、腐蚀的类型以及点蚀深度等。金属挂片的数据除受腐蚀介质影响外，还与挂片表面处理、放置部位、暴露时间长短以及样片冶金方式等因素有关。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条