1) adhesive wear
粘结磨损
1.
It is found that the cermet tools exhibite higher wear resistance for cutting austenite stainless steel and adhesive wear is the main source of tools failure.
结果表明:纳米复合Ti(C,N)基金属陶瓷刀片在切削奥氏体不锈钢时表现出较高的耐磨性,其主要的磨损失效机理为粘结磨损,同时伴随一定的氧化磨损和扩散磨损。
2.
During turning,the cutting temperature of rake face was higher than that of flank face,so adhesive wear.
研究结果表明,使用硬质合金刀具材料高速干车削Ti-6Al-4V时,刀具的磨损机理主要为粘结磨损、氧化磨损和扩散磨损。
2) adhesive wear
粘着磨损
1.
Results show that the wear rate of O'-Sialon-ZrO2-SiC is much less than that of stainless steel at the testing condition, and main wear mechanism of the unlubricated friction is adhesive wear.
研究表明，在实验条件下，O′－Sialon－ZrO2－SiC复合材料的磨损率远低于不锈钢的磨损率，O′-Sialon-ZrO2－SiC／不锈钢摩擦副间的磨损机制主要是粘着磨损。
2.
It is found that the wear mechanism between O '-sialon-ZrO 2-SiC composite and stainless steel is mainly of adhesive wear under dry condition.
室温干摩擦条件下，磨损机制以粘着磨损为主。
3.
It has been found that the wear mechanisms of O′ Sialon ZrO 2 SiC composite/1Cr13 steel pair were dominated by adhesive wear and abrasive wear under dry sliding, while the fluctuation of the friction coefficient was large.
结果表明：在６００ ℃干摩擦条件下， Ｏ′ Ｓｉａｌｏｎ Ｚｒ Ｏ２ Ｓｉ Ｃ 复合材料的磨损质量损失远低于１ Ｃｒ１３ 钢的磨损质量损失； Ｏ′ Ｓｉａｌｏｎ Ｚｒ Ｏ２ Ｓｉ Ｃ 复合材料／１ Ｃｒ１３ 钢摩擦副的摩擦系数波动较大，磨损机制以粘着磨损和磨粒磨损为
3) adhesion
[英][əd'hi:ʒn] [美][əd'hiʒən]
粘着磨损
1.
A study on the effect of micro addition rare earth elements and chromium on adhesion behavior of boronized layer,Fe 2B phase,has been made using an MM 200 wear tester.
研究了微量稀土元素和铬对Fe2 B单相渗硼层粘着磨损特性的影响。
4) Adhesion wear
粘着磨损
1.
The mechanism of hot-dipped aluminum is mainly adhesion wear,and that of complex boroned after hot-dipped aluminum is primarily abration wear with adhesion.
热浸渗铝的磨损机制以粘着磨损为主;而热浸渗铝复合渗硼以磨粒磨损为主要机制,同时伴有粘着磨损。
2.
So,the experiments on adhesion wear and erosion wear are done,and the wear weight are measured by weighing method of samples.
NM 360是在Q 345基础上通过调整合金元素后生产的新钢种,还缺少摩擦磨损性能的评定参数,通过粘着磨损和冲蚀磨损试验用称重法测量其磨损量,测定了它的抗粘着和抗冲蚀的摩擦学性能,试验结果表明微量合金元素能改善材料组织,其性能优于Q 345,并与国外同类产品的性能相当。
3.
The results show adhesion wear occurred at both friction couples.
对A型发射装置,进行了大量的验证试验,并对锁制机构进行了理论计算和摩擦副表面扫描电镜观察;对B型发射装置的运动副表面形貌进行了分析,结果表明二者摩擦副均发生了粘着磨损。
5) tacky rub-off
粘性磨损
6) adhesive wear
胶粘磨损
补充资料：HJ-1水产饲料粘结剂
分子式：
分子量：
CAS号：
性状：白色粉末。
用途：是一种高分子型粘合剂。用作鱼虾饵料粘合剂，用量仅为饲料量的0.5%。粘合性能好。被粘接的颗粒饲料在水中保形时间大于2小时，达到鱼虾粘合剂的指标。也可用作鸡、猪、牛等配合饲料粘结剂。
制备或来源：以尿素、醛、醇为原料，经反应改性后，即得本品。
类别：粘结剂
分子量：
CAS号：
性状：白色粉末。
用途：是一种高分子型粘合剂。用作鱼虾饵料粘合剂，用量仅为饲料量的0.5%。粘合性能好。被粘接的颗粒饲料在水中保形时间大于2小时，达到鱼虾粘合剂的指标。也可用作鸡、猪、牛等配合饲料粘结剂。
制备或来源：以尿素、醛、醇为原料，经反应改性后，即得本品。
类别：粘结剂
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条