1) aluminum pretanning
铝预鞣
2) aluminium tanning
铝鞣
1.
The methods of chrome tanning and aluminium tanning are contrasted in this article.
对铬鞣法和铝鞣法进行了对比 ,介绍了少铬的一些铬铝结合鞣法及铬铝鞣剂的几种生产方法 ;说明了铬铝鞣制在清洁制革工艺上的作用及优点。
2.
The factors,affecting the performances of aluminium tanned pigskin leather,such as dosage of chromium -free additive D and aluminium tanning agent,pH and time were investigated.
以猪皮酸皮进行鞣制试验,通过研究无铬鞣伴侣D用量、pH值、时间、鞣剂用量对铝鞣革性能的影响,得出了使用铝鞣剂与无铬鞣伴侣D的较佳鞣制工艺。
3) pretanning
预鞣
1.
The new technology about THP/mimosa pretanning and high activity fish oil tannage,can reducehalf tanning time comparing with the traditional oil tannage.
四羟甲基季鏻盐(THP盐)、栲胶预鞣、高活性鱼油油鞣的鞣革新工艺,较传统油鞣工艺时间缩短一半,所得成革为可水洗软革,收缩温度为86℃(传统油鞣工艺大约65℃),抗张强度为23。
2.
The optimal pretanning results can obtain at prescription of 7% THP and 6% oxazolidine; the optimum conditions for the chamoising process is as follows:high active fish oil 50%,temperature 40℃,humidity 80%,tanning time 25h.
四羟甲基季鏻盐(THP盐)、噁唑烷预鞣、高活性鱼油油鞣的鞣革新工艺,较传统油鞣工艺时间缩短一半,所得成革为可水洗软革,收缩温度为85℃(传统油鞣工艺大约65℃),抗张强度为30。
4) aluminium tanning agent
铝鞣剂
1.
The content of aluminium oxide was determinaed in aluminium tanning agent by use of chelatometric titration method under the various titration conditions.
采用络合滴定法 ,在各种不同的滴定条件下 ,对铝鞣剂中三氧化二铝含量进行检测 ,确定了最佳的检测条件。
2.
This tanning agent can not only overcome “pale shade” shortcoming of acrylic resin, but also improve Ts and washing fastness of leather tanned with aluminium tanning agent.
采用溶液聚合的方法对丙烯酸单体进行聚合 ,然后再与铝离子配合 ,生成一种配合物鞣剂 ,该鞣剂克服了丙烯酸树脂类鞣剂的“败色”现象 ,在一定程度上克服了铝鞣剂收缩温度不高、不耐水洗的缺点 ,既体现了丙烯酸树脂对皮革填充性好、丰满的优点 ,也体现了铝鞣剂鞣革柔软、纯白、粒面细致而紧实、延伸性好的优点 。
6) chrome and aluminium tanning agent
铬铝鞣剂
补充资料：硝铝鞣
分子式：
CAS号：
性质：又称矾鞣或铝鞣。用钾明矾、铵明矾、硫酸铝等鞣制毛皮的方法。鞣得的皮毛洁白柔软、延伸性好，但耐洗性和耐热性很差，已被铬铝鞣或醛铝结合鞣取代它作为主鞣的地位，现今只常作油鞣和某些增色细毛皮的预鞣。硝铝鞣的毛皮在后面再加踢皮油处理，可提高产品质量，常用于生产中、高档毛皮，亦称油鞣。
CAS号：
性质：又称矾鞣或铝鞣。用钾明矾、铵明矾、硫酸铝等鞣制毛皮的方法。鞣得的皮毛洁白柔软、延伸性好，但耐洗性和耐热性很差，已被铬铝鞣或醛铝结合鞣取代它作为主鞣的地位，现今只常作油鞣和某些增色细毛皮的预鞣。硝铝鞣的毛皮在后面再加踢皮油处理，可提高产品质量，常用于生产中、高档毛皮，亦称油鞣。