1) aluminium tannage
铝鞣法
2) aluminium tanning
铝鞣
1.
The methods of chrome tanning and aluminium tanning are contrasted in this article.
对铬鞣法和铝鞣法进行了对比 ,介绍了少铬的一些铬铝结合鞣法及铬铝鞣剂的几种生产方法 ;说明了铬铝鞣制在清洁制革工艺上的作用及优点。
2.
The factors,affecting the performances of aluminium tanned pigskin leather,such as dosage of chromium -free additive D and aluminium tanning agent,pH and time were investigated.
以猪皮酸皮进行鞣制试验,通过研究无铬鞣伴侣D用量、pH值、时间、鞣剂用量对铝鞣革性能的影响,得出了使用铝鞣剂与无铬鞣伴侣D的较佳鞣制工艺。
3) Dongola tannage
铝-槟榔膏结合鞣法
4) aluminum pretanning
铝预鞣
5) aluminium tanning agent
铝鞣剂
1.
The content of aluminium oxide was determinaed in aluminium tanning agent by use of chelatometric titration method under the various titration conditions.
采用络合滴定法 ,在各种不同的滴定条件下 ,对铝鞣剂中三氧化二铝含量进行检测 ,确定了最佳的检测条件。
2.
This tanning agent can not only overcome “pale shade” shortcoming of acrylic resin, but also improve Ts and washing fastness of leather tanned with aluminium tanning agent.
采用溶液聚合的方法对丙烯酸单体进行聚合 ,然后再与铝离子配合 ,生成一种配合物鞣剂 ,该鞣剂克服了丙烯酸树脂类鞣剂的“败色”现象 ,在一定程度上克服了铝鞣剂收缩温度不高、不耐水洗的缺点 ,既体现了丙烯酸树脂对皮革填充性好、丰满的优点 ,也体现了铝鞣剂鞣革柔软、纯白、粒面细致而紧实、延伸性好的优点 。
补充资料：铝鞣法
分子式：
CAS号：
性质：一种历史悠久的鞣革方法。三价碱式铝盐鞣制的革颜色洁白、柔软，粒面细致，称为铝鞣革(alumitanned leather)。在铬鞣发明以前，铝鞣曾是一种主要的无机鞣法，后来被铬鞣取代了它的地位，原因是铝络合物只与胶原的羧基发生单点结合，鞣性不强。铝鞣革的收缩温度只达到70～75℃，铝盐易水解，铝鞣革遇水易退鞣变硬，失去使用价值。铝盐虽不宜单独鞣革，但与铬盐、植物鞣剂或合成鞣剂作结合鞣，能改善鞣革性能，前景良好。
CAS号：
性质：一种历史悠久的鞣革方法。三价碱式铝盐鞣制的革颜色洁白、柔软，粒面细致，称为铝鞣革(alumitanned leather)。在铬鞣发明以前，铝鞣曾是一种主要的无机鞣法，后来被铬鞣取代了它的地位，原因是铝络合物只与胶原的羧基发生单点结合，鞣性不强。铝鞣革的收缩温度只达到70～75℃，铝盐易水解，铝鞣革遇水易退鞣变硬，失去使用价值。铝盐虽不宜单独鞣革，但与铬盐、植物鞣剂或合成鞣剂作结合鞣，能改善鞣革性能，前景良好。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。