1) delayed propagation
滞后扩展
1.
Results showed that the residual stress itself was not enough to induce delayed propagation of the crack when the relative humidity was small(RH≤30%).
在不同湿度(2%、30%、98%)的空气中,研究了极化的锆钛酸铅(PZT-5)铁电陶瓷压痕裂纹在残余应力、电场作用下的滞后扩展。
2.
The residual stress of the unloaded indentation crack can induce crack delayed propagation and domain switching in humid air and water.
原位研究了残余应力和外加应力导致 BaTiO_3单晶压痕裂纹在湿空气和水中的滞后扩展及畴变。
3.
The experiment of a coupling effect on propagation of unloaded indentation cracks in a PZT-5H ceramic shows that residual stress itself is too small to induce delayed propagation of the indentation crack in silicon oil.
结果表明,残余应力不足以使压痕裂纹在硅油中发生滞后扩展,只有外加恒电场E>0。
2) hydrogen-induced delayed cracking
氢致滞后扩展
3) Extended game with observable delay
可观测滞后扩展博弈
4) backward development
发展滞后
1.
But horizontally there are many factors leading to its backward development.
改革开放以来,安徽省的对外工程承包和劳务合作获得了较快发展,但从横向来讲仍存在发展滞后问题。
5) stagnate development
滞后发展
1.
Among the different views about the development of urbanization in China, the view of stagnate development is the dominant.
本文归纳总结了对中国城市化发展水平的不同意见 ,对占主流的“滞后发展”的观点进行了分析评价 ,指出其存在方法论的缺陷。
6) microcrack arrest
微裂纹扩展阻滞
补充资料：弹性滞后
分子式：
CAS号：
性质：一种动态黏弹性现象，即聚合物在交变应力(应力大小呈周期性的变化)作用下，形变的变化总是滞后于应力的变化。产生该现象的主要原因是聚合物受外力后，其链段的运动要克服内摩擦力，从一种状态过渡到与外力相适应的状态需要一定时间，故形变不能立即产生；同样当外力除去后，形变也不能马上回复。弹性滞后使汽车轮胎、橡胶传送带、塑料齿轮等制品产生力学阻尼(内耗)等动态黏弹性现象。
CAS号：
性质：一种动态黏弹性现象，即聚合物在交变应力(应力大小呈周期性的变化)作用下，形变的变化总是滞后于应力的变化。产生该现象的主要原因是聚合物受外力后，其链段的运动要克服内摩擦力，从一种状态过渡到与外力相适应的状态需要一定时间，故形变不能立即产生；同样当外力除去后，形变也不能马上回复。弹性滞后使汽车轮胎、橡胶传送带、塑料齿轮等制品产生力学阻尼(内耗)等动态黏弹性现象。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条