1) sialon block
sialon块体
2) SiAlON polytypoids
多型体SiAlON
1.
Effects of SiAlON polytypoids contents on the bulk density, apparent porosity and room and high temperature modulus of rup- ture were investigated.
以电熔白刚玉、矾土细粉、铝(Al)粉和硅(Si)粉为原料,通过原位氮化反应烧结工艺在较低温度(1500℃)下制备了多型体SiAlON[12H(SiAl5O2N5),21R(SiAl6O2N6)]结合刚玉耐火材料。
3) β'-Sialon powders
β'-Sialon粉体
1.
The favourite temperature was discussed for acquiring more β'-Sialon powders.
本文分析了以天然高岭土为原料，经碳热还原氨化反应制备β′-Sialon粉体过程中出现的化学反应，从热力学角度研究了反应温度及气体分压对产物组成的影响，通过实验结果与热力学分析相结合，寻找出制约反应进行的速度控制步骤，并讨论了获得较高β′-Sialon粉体转化率所需的温度范围。
5) Sialon-corundum composite powder material
β-Sialon/刚玉复相粉体材料
6) sialon
['saiəlɔn]
α-Sialon
1.
The effects of various experimental paramete rs on combustion synthesis of single phase Ybá-sialon powders characterized by o ne-dimension elongated morphology have been measured.
研究了各参数对燃烧合成长柱状Ybα-Sialon相组成及形貌的影响。
补充资料：高温超导体块材组织结构
高温超导体块材组织结构
microstructure of the bulk high temperature superconductor
高温超导体块材组织结构mierostrueture of thebulk high temPerature supereonduetor高温超导体的相组成、晶粒形貌和尺寸，以及与超导电性关系密切的冶金缺陷和晶体缺陷。块材是指薄膜和纤维之外的三维大尺寸材料。 1986年以来陆续发现的高临界转变温度Tc超导体是一个具有陶瓷特性的庞大家族。除Tc高之外，还有很多不同于传统低Tc超导体的共同特征:它们大多具u)为化学全部有超;即的多二uo犷望，叮类。晶块为片和铺这些质相卜、杂和原常常1988Zn)、薄膜约晶Cu、杂相 贫a一b超流角为:值。在相目肠样密度匀单靠实有畸变的层状钙钦矿结晶结构;成分多是以铜((主要元素的金属氧化物，氧含量和含铜材料中铜跳价态都具有不确定性;化合物中大多数金属元素司或部分被其他金属元素替代而不明显改变或仍然具导电性;晶体结构和超导电性具有明显的各向异性使在同一种超导体中，往往共生着结构和Tc各异种超导相。BISrCaCuO(BSCCO)、YBa((YBCO)和TIBaCaCuO(TBCCO)系最有实用矛而被研究得最多的是BSCCO和YBCO超导体。 块材晶粒排列从组织形态上块材可分以下了①晶粒随机取向多晶块:晶轴取向呈无规排列的多材。又称颗粒超导体。秘(Bi)系多晶块中的晶粒状，c轴平行于片的厚度方向;忆(Y)、锭(TD(La)系块材晶粒形状类似，为等轴或棒状晶。在多晶材料中，往往含有少量的非超导金属氧化物杂和孔洞。体密度为理论密度的70一95%。晶粒尺二相和孔洞所占的体积分数和分布状态，与制作工艺始粉末粒度、坯料的成分均匀度有关。在晶界附近，可观察到由热加工过程中应力集聚产生的微裂纹。年和1990年，美国的D.拉巴勒斯蒂(LarbalestiD.戴莫斯(Dimos)等人先后分别对忆系烧结块和双晶作了深入的研究。在烧结块中，有75%以上界是清洁无杂相的，其余不到25%的晶界为含富贫Y、贫钡(Ba)和氧(O)的杂相薄层;即使是无的晶界，其两侧snln的短程区也是富Cu、贫BaO的。