1) welding on dissimilar steel
异质钢焊接
3) dissimilar weld
异种钢焊接
1.
Microstructure and properties of dissimilar weldment between duplex stainless steel and micro-alloyed steel;
采用ER2209焊丝对双相不锈钢SAF2205与微合金管线钢X65进行熔化极气体保护焊接,获得了具有良好力学性能的异种钢焊接接头。
4) dissimilar steel welding
异种钢焊接
1.
With the detailed repairing scheme, a dissimilar steel welding technique about 45 steel and 20 steel under the condition of temperature and sharp cooling is brought forward and gets success.
提出了在室温急冷的条件下，４５钢与２０钢异种钢焊接的工艺措施，并取得成功。
2.
Along with the development of modern industry, new technologies, dissimilar steel welding is widely used in variant engineering fields.
随着现代工业的飞速发展,异种钢焊接而成的复合零部件在各种工程领域有着日益广泛的应用。
5) Dissimilar Steel Weld
异种钢焊接
1.
It is deemed that the dissimilar steel welding between the locating piece and reheater tubes and unproper structure of the location piece are the major reason that causes the tube leakage.
分析了再热器管频繁泄漏的原因,认为定位块与再热器管的异种钢焊接及定位块结构的不合理是导致泄漏的主要原因,同时提出了改造方案。
6) dissimilar steel welded joint
异种钢焊接接头
1.
Using the T91 filler metals and by the means of TIG process ,the over matched dissimilar steel welded joint of T91 and 12Cr1MoV was made.
对高强匹配的T91/12Cr1MoV异种钢焊接接头分别进行常温力学性能和高温持久试验 ,试验结果表明 ,常温拉伸试样均断在 12Cr1MoV母材侧 ,接头的强度高于 12Cr1MoV母材 ;接头中焊缝的硬度值最高 ,为 3 17HV ;焊缝常温下的冲击韧性为 86kJ/cm2 ,高于 12Cr1MoV母材 ;接头的高温持久性能明显低于 12Cr1MoV母材 ,失效位置 (接头的薄弱环节 )在 12Cr1MoV侧的熔合线附近。
补充资料：钢质焊接气瓶
分子式：
CAS号：
性质： 由圆柱形简体和顶、底部凸形封头(椭圆形或碟式)焊接组成，并且简体纵焊缝不得多于一条，环焊缝不得多于三条。选材必须采用平炉、电炉或氧气转炉冶炼的镇静钢。焊接气瓶主要盛装低压液化气体和溶解气体，由于气瓶系移动式压力容器，故其选材、制造、检验、使用等必须严格按有关标准执行，确保安全使用。
CAS号：
性质： 由圆柱形简体和顶、底部凸形封头(椭圆形或碟式)焊接组成，并且简体纵焊缝不得多于一条，环焊缝不得多于三条。选材必须采用平炉、电炉或氧气转炉冶炼的镇静钢。焊接气瓶主要盛装低压液化气体和溶解气体，由于气瓶系移动式压力容器，故其选材、制造、检验、使用等必须严格按有关标准执行，确保安全使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条