1) dissimilar materials joint
异质焊接接头
2) heterogeneous joint
异质接头
1.
The heterogeneous joints of Cr5Mo processing pipelines,which served under five different operation conditions in reforming equipment,are taken as the objects to research the effects of different operation temperatures on the structures and characteristics.
以某炼油厂重整装置5种不同工况的Cr5Mo工艺管道异质接头为对象,研究了不同操作温度对异质接头组织和性能的影响。
3) dissimilar welding joint
异种焊接接头
4) dissimilar steel welded joint
异种钢焊接接头
1.
Using the T91 filler metals and by the means of TIG process ,the over matched dissimilar steel welded joint of T91 and 12Cr1MoV was made.
对高强匹配的T91/12Cr1MoV异种钢焊接接头分别进行常温力学性能和高温持久试验 ,试验结果表明 ,常温拉伸试样均断在 12Cr1MoV母材侧 ,接头的强度高于 12Cr1MoV母材 ;接头中焊缝的硬度值最高 ,为 3 17HV ;焊缝常温下的冲击韧性为 86kJ/cm2 ,高于 12Cr1MoV母材 ;接头的高温持久性能明显低于 12Cr1MoV母材 ,失效位置 (接头的薄弱环节 )在 12Cr1MoV侧的熔合线附近。
5) welding on dissimilar steel
异质钢焊接
补充资料：焊接接头晶间腐蚀
焊接接头晶间腐蚀
welded joint intercryctalline corrosion
honjle」}etou jingj旧n fush{焊接接头晶间腐蚀(welded joint intererys-talline eorrosion)在焊接接头处出现的沿晶粒边界发生的腐蚀现象。外观仍可有金属光泽，但实际上晶粒已失去联系，钢质已变脆。在奥氏体不锈钢部位有焊缝晶间腐蚀、敏化区腐蚀和刀状腐蚀等三种不同部位的晶间腐蚀。关于奥氏体不锈钢的晶间腐蚀机理有多种学说，其中以碳化物(如er23e。或(er、Fe)23e。等)在晶界沉淀现象的“贫铬理论”比较为人们所接受。所以为防止这类晶间腐蚀尽量降低含碳量，使焊缝金属含有一定量的稳定元素(如钦、妮等)以防止或降低晶界Cr23C。的形成。此外，焊缝的组织状态也有影响，单相奥氏体组织的焊缝有利于柱状晶的发达，出现贫铬层后会使腐蚀贯穿于晶粒之间，若焊缝为奥氏体了加高温铁素体占的双相组织，由于树枝状被打破，不能构成集中的腐蚀通道。高铬铁素体也会有晶间腐蚀，但与奥氏体钢不同的是从高温急冷下来即有晶间腐蚀倾向，可通过650一85oC加热、缓冷使铬扩散均匀化来消除贫铬层，防止晶间腐蚀。 (许祖泽)