1) body
[英]['bɔdi] [美]['bɑdɪ]
坯体
1.
Research on low temperature fast single-firing body for glazed tile using coal gangue
煤矸石为主一次低温快烧琉璃瓦坯体的研究
2.
Study on sintering mechanism of fired tile body with shale
页岩烧结瓦坯体烧结机理研究
3.
Some discussions on the development of drying equipment in daily-use ceramic industry and drying technology of ceramic body.
对日用陶瓷工业的干燥设备发展及陶瓷坯体干燥技术的发展进行论述,认为随着干燥设备的进一步优化和改进,坯体的干燥将向快速、高效、节能及环保的方面发展。
2) green body
坯体
1.
After sieving, prilling and vibrating packing, the green body has been pressed.
044mm)和聚乙烯醇水溶液(PVA,其中聚乙烯醇质量份数为5%)按一定比例混匀,过筛造粒,振动装料后进行冷等静压成型,研究了水分和PVA含量对硅粉坯体成型和性能的影响。
2.
The results show that machined depth was increased with the increase of electric current and decreased with the increase of machining speed and scanning gap for the green body prepared by the same forming.
对不同成型方法(包括干压成型、流延成型、凝胶注模成型、注射成型等)得到的氧化铝陶瓷坯体进行激光加工,讨论成型方法对激光加工陶瓷坯体效率的影响。
3) bodyware
坯体
1.
Relations Between Coefficient of Expansion and Chemical Composition for Raw Material and Mixture of Bodyware in Ceramics Tile;
陶瓷墙地砖坯体原料和混合物膨胀系数与化学成分的关系
2.
Optimizing Limits of Ingredient for Bodywares of Porcelian Tiles;
瓷质砖坯体配方优化范围
4) preform
[英][pri:'fɔ:m] [美][pri'fɔrm]
坯体
1.
Study on preform of carbon/carbon composites for aircraft brakes;
航空刹车用C/C复合材料坯体结构研究
2.
In order to find effective ways of lowering cost of C/C composites for aircraft brakes and improving their performances, some mechanical performances and thermal properties of foreign composites were measured and their preforms were detected.
为了探索降低航空刹车用C/C复合材料成本、提高性能的有效方法 ,对现役国外航空刹车用C/C复合材料的部分力学性能和热导率进行测试 ,并利用金相显微镜对其坯体结构进行观察分析 ,在此基础上 ,自制了一种针刺整体毡 ,进行CVD增密 ,并与炭布叠层坯体的结果对比。
5) green strength
坯体强度
1.
Effects of process parameters on the gelcasting green strength and sintered density of stainless steel;
工艺参数对凝胶注模成型不锈钢坯体强度和烧结密度的影响
6) ceramic body
陶瓷坯体
1.
This paper introduces the prescription design of the ceramic body with the lower sintering temperature.
通过对水玻璃、废玻璃和三聚磷酸钠进行物理、化学性质分析,利用废玻璃代替部分水玻璃进行低温陶瓷坯体配方设计,获得性能较好且烧成温度为860oC左右的低温陶瓷坯体。
补充资料：坯体
分子式：
CAS号：
性质：又称坯体或生坯。指借助于外力和模型，将泥料加工成型为具有一定形状、尺寸和强度并可用于烧成的中间产品。未经干燥的称为湿坯，干燥后的称为干坯。成型后不经烧成可直接使用的制品称为不烧砖。在耐火材料的生产中，砖坯的质量技术指标有砖坯的尺寸和外形、单重、密度、气孔率以及强度等。
CAS号：
性质：又称坯体或生坯。指借助于外力和模型，将泥料加工成型为具有一定形状、尺寸和强度并可用于烧成的中间产品。未经干燥的称为湿坯，干燥后的称为干坯。成型后不经烧成可直接使用的制品称为不烧砖。在耐火材料的生产中，砖坯的质量技术指标有砖坯的尺寸和外形、单重、密度、气孔率以及强度等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条