1) surface decarbonization
表面脱碳
1.
The technique by which surface decarbonization of Shaw process castings can be completely eradicated was introduced in detail, and the theory is discussed.
详细介绍了一种根治陶瓷型铸件表面脱碳的方法并分析其原理。
2.
Metallurgical defects, heat-treated defects and surface decarbonization cause the fatigue fracture jointly.
结果表明,吊车车轮断裂为疲劳断裂,表面脱碳、冶金缺陷以及热处理缺陷是导致吊车车轮疲劳断裂的三个主要原因。
2) surface decarburization
表面脱碳
1.
The surface decarburization for steel 60Si2Mn is more serious than for 5160H, because the carbon activity is increased by silicon.
Ｓｉ增加奥氏体中碳的活度使６０Ｓｉ２Ｍｎ钢表面脱碳较５１６０Ｈ严重。
2.
The effect of heating temperature on the surface decarburization of 60Si2Mn spring steel is calculated theoretically in consideration of factors like carbon diffusion and oxidation.
表面脱碳是高速线材生产的重要问题之一。
3) surface decarburation
表面脱碳作用
4) superficial decarbonization
表层脱碳
1.
The results indicate that superstandard inclusion of material,which leads to primary microcrack at moveing round confectioning,is the principal reason of the crack under 100KN force,superficial decarbonization at heat-treating decreases the admission compression force of crack.
结果表明:原材料内部夹杂物超标是导致产品在绕弯成形时产生初生裂纹,并在热处理后于规定100kN压力试验时产生开裂的主要原因,热处理过程中产生的表层脱碳降低了产品产生开裂的允许压力。
5) Surface Recarburization
表面增碳
1.
Surface Recarburization of Wear-resistant Bainite Steel Castings in Lost Foam Casting;
消失模贝氏体钢耐磨铸件表面增碳问题
6) Surface Carbonization
表面渗碳
1.
Effect of Mould Shielded Fluxes on Concasting Billet Surface Carbonization of Ultra-Low-Carbon Steel;
结晶器保护渣对超低碳钢连铸坯表面渗碳的影响
补充资料：氟碳表面活性剂
分子式：暂无
分子量：暂无
CAS号：暂无
性质：暂无
制备方法：暂无
用途：暂无
分子量：暂无
CAS号：暂无
性质：暂无
制备方法：暂无
用途：暂无
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条