1) emulsion blend
乳液共混
1.
A water-swellable NR(WSNR) was prepared by blending liquid starch-g-polymethyl acrylic acid(SPMAA) directly with NR latex based on emulsion blending method,and the influence of SPMAA and montmorillonite(MMT) on the water absorption and physical properties of WSNR vulcanizate was investigated.
利用乳液共混法将淀粉接枝聚甲基丙烯酸(SPMAA)在液态下直接与天然胶乳共混制备吸水膨胀NR(WSNR),并研究SPMAA和蒙脱土对WSNR硫化胶吸水性能和物理性能的影响。
2) Blending emulsion
共混乳液
1.
This paper introduces the polysiloxane/acrylate blending emulsion,copoly-mer emulsion and composite emulsion.
详细介绍了聚硅氧烷/丙烯酸酯共混乳液、共聚乳液及复合乳液。
3) latex compounding
乳液共混法
1.
The palygorskite/natural rubber composites were prepared by latex compounding.
本实验采用乳液共混法制备了坡缕石／天然橡胶复合材料,并对复合材料进行了表征。
4) co-coagulating rubber latex
乳液共混共凝
1.
Attapulgite/natural rubber composites (ANRC) were prepared by co-coagulating rubber latex and clay aqueous suspension.
采用乳液共混共凝法制备了凹凸棒石/天然橡胶复合材料(attapulgite/natural rubber composites,ANRC),并对ANRC进行了表征。
5) mixing and co-coagulating
乳液共混共凝法
1.
This experiment prepared the silane modifying attapulgite/natural rubber composites(ANRC) by the method of mixing and co-coagulating.
硅烷改性凹凸棒石后,采用乳液共混共凝法制备出了凹凸棒石/天然橡胶复合材料(attapulgite/natural rub-ber composites,ANRC),并对ANRC进行了表征;红外光谱分析证实凹凸棒石得到了有机化改性;ANRC的力学性能测试表明,当天然胶乳浓度适宜?改性剂用量为1。
补充资料：乳液共混
分子式：
CAS号：
性质：将不同聚合物乳液一起搅拌均匀后，加入凝聚剂使异种聚合物共沉析以形成聚合物共混物体系。此法可保证共混产物的均匀性，但仅能适用于乳液法生产的品种。当原料聚合物为聚合物乳液、胶液或共混物以乳液形式被利用时，此法最为有利。常与共聚-共混法联用，也可作为熔融共混的预备性操作。主要优点是它能够接枝和交联，控制粒度分布，控制共单体的用量比。缺点是它需要铁和其他过渡金属元素作为氧化还原引发体系的组分。这些金属离子必须彻底洗净，否则树脂将在干燥或加工成型过程中发生降解。
CAS号：
性质：将不同聚合物乳液一起搅拌均匀后，加入凝聚剂使异种聚合物共沉析以形成聚合物共混物体系。此法可保证共混产物的均匀性，但仅能适用于乳液法生产的品种。当原料聚合物为聚合物乳液、胶液或共混物以乳液形式被利用时，此法最为有利。常与共聚-共混法联用，也可作为熔融共混的预备性操作。主要优点是它能够接枝和交联，控制粒度分布，控制共单体的用量比。缺点是它需要铁和其他过渡金属元素作为氧化还原引发体系的组分。这些金属离子必须彻底洗净，否则树脂将在干燥或加工成型过程中发生降解。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。