1) Hot pressure casting
热压铸
1.
Using fine powders of lithium aluminate synthesized by the solid-state reaction as the starting materials, porous thin-wall tubelike specimens were fabricated by the improved hot pressure casting method.
以固相反应法合成出的LiAlO2细粉作为原料,采用改进的热压铸活塞法压制出薄壁管生坯,并对脱蜡后的素坯进行微波烧结与常规烧结两种不同工艺试验的比较,从产氚机理、粉体煅烧温度、颗粒尺寸、表面活性剂种类和烧结工艺等方面展开了较为系统的研究。
2) hot chamber die casting
热室压铸
1.
The hot chamber die casting is a traditional die casting method,and there are several things that must be paid attention during the installation and operation of the hot chamber die casting machines.
热室压铸机压铸是一种传统的压铸方法,在压铸生产中有一些值得注意之处。
4) Heat-Pressed Ceramic
热压铸瓷
1.
Influence of Resin Cement Thickness on the Color of Heat-Pressed Ceramic System;
树脂粘接剂的厚度对热压铸瓷修复体颜色的影响
6) hot chamber die casting machine
热室压铸机
1.
Optimization design of hot chamber die casting machine based on ADAMS;
基于ADAMS的热室压铸机机铰优化设计
2.
Improved Design on Reliability of J213B Hot Chamber Die Casting Machine;
J213B型热室压铸机可靠性改进设计
补充资料：热压铸成型
分子式：
CAS号：
性质：将瓷料和熔化的蜡类黏结剂，经搅拌混合均匀，倒入热压铸机，用压缩空气把加热熔化的料浆压入金属模腔，使料浆在模具内凝固成型。热压铸成型用的蜡类黏结剂，通常为石蜡，为改善料浆的流动性，减少石蜡用量可加入少量(0.5%～5%)的表面活性物质如油酸、蜂蜡、硬脂酸等。黏结剂含量一般为瓷料重量的10%～18%。成型时料浆温度为50～85℃，压缩空气压力比0.1～0.5MPa，通常大型制品料浆温度和空气压力偏高。此法优点是：操作简便，可成型各种形状复杂的制品，生坯的强度高、表面光洁度好，模具磨损小，劳动生产率较高，但坯件致密度较低，烧成前需要有脱蜡工序，对致密度要求高的制品常难满足要求。
CAS号：
性质：将瓷料和熔化的蜡类黏结剂，经搅拌混合均匀，倒入热压铸机，用压缩空气把加热熔化的料浆压入金属模腔，使料浆在模具内凝固成型。热压铸成型用的蜡类黏结剂，通常为石蜡，为改善料浆的流动性，减少石蜡用量可加入少量(0.5%～5%)的表面活性物质如油酸、蜂蜡、硬脂酸等。黏结剂含量一般为瓷料重量的10%～18%。成型时料浆温度为50～85℃，压缩空气压力比0.1～0.5MPa，通常大型制品料浆温度和空气压力偏高。此法优点是：操作简便，可成型各种形状复杂的制品，生坯的强度高、表面光洁度好，模具磨损小，劳动生产率较高，但坯件致密度较低，烧成前需要有脱蜡工序，对致密度要求高的制品常难满足要求。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。