1) Fe-Al/SiC composite coating
Fe-Al/SiC复合涂层
1.
Fe-Al/SiC composite coating was made by HVFS.
利用高速火焰喷涂技术制备出Fe-Al/SiC复合涂层,在MM-A1立式磨损试验机上对涂层常温下的摩擦磨损特性进行研究。
2.
It indicated that the matrix of Fe-Al/SiC composite coating was Fe-Al phase (Fe3Al,FeAl) and SiC hard phase distributed all over the coating, and the coating displayed the typical layers structure characteristics.
采用高速火焰喷涂技术制备了Fe-Al/SiC复合涂层,对涂层在650℃下的热腐蚀动力学规律进行了研究,并利用扫描电镜(SEM)、能谱仪(EDS)和X射线衍射仪(XRD)对涂层及腐蚀产物的成分和形貌进行分析。
3.
In order to solve the hot corrosion problem on the water-wall tubes in thermal power plants, HVFS technology was used to prepare the Fe-Al/SiC composite coating, and the bonding strength, micro hardness, thermal shock and hot corrosive resistance performance of the coating were studied.
为解决火电厂锅炉水冷壁热腐蚀问题,采用高速火焰喷涂技术首次制备出Fe-Al/SiC复合涂层,并对涂层的结合强度、显微硬度、抗热震性能和耐热腐蚀性能进行了研究。
2) Fe-Al/Cr_3C_2 composite coating
Fe-Al/Cr3C2复合涂层
3) iron-aluminide and alumina composite coating
Fe-Al/Al2O3复合涂层
5) Fe-Al/WC composite coating
Fe-Al/WC复合涂层
1.
The Fe-Al/WC intermetallic composite coatings have been prepared by high velocity arc spraying (HVAS)technology on 20G steel and the anti-hot corrosion performance of Fe-Al/WC composite coatings at 450℃ has been studied by hot corrosion test.
结果表明,Fe-Al/WC复合涂层的热腐蚀动力学曲线近似呈现出抛物线规律;涂层表面的腐蚀产物主要为疏松的Fe2O3,此外,还有少量的Al2O3和FeS,且其分布不均匀;涂层表面优先形成具有保护性的Al2O3膜,保证了涂层具有一定的抗热腐蚀性能;Fe元素的扩散、化学反应及电化学反应综合作用是涂层加速腐蚀的主要原因。
6) Fe-Al alloy coatings
Fe-Al合金涂层
补充资料：等离子喷涂羟基磷灰石涂层-钛复合材料
分子式：
CAS号：
性质：是用等离子喷涂技术在医用金属钛或其合金表面加涂羟基磷灰石所制得的医用涂层材料。主要用于承力部位的硬组织修复和替换，如制作人工种植牙、关节柄和接骨板等。由于表面涂层赋予了表面生物活性，植入骨内后能与骨直接形成骨键合，手术中可不用骨水泥固定。为使涂层能在生物环境中保持稳定和涂层-基体界面具有足够的结合强度，要求涂层的羟基磷灰石含量达90％以上并具有高的结晶度。另外，钴基合金也可作为这种涂层材料的基材。
CAS号：
性质：是用等离子喷涂技术在医用金属钛或其合金表面加涂羟基磷灰石所制得的医用涂层材料。主要用于承力部位的硬组织修复和替换，如制作人工种植牙、关节柄和接骨板等。由于表面涂层赋予了表面生物活性，植入骨内后能与骨直接形成骨键合，手术中可不用骨水泥固定。为使涂层能在生物环境中保持稳定和涂层-基体界面具有足够的结合强度，要求涂层的羟基磷灰石含量达90％以上并具有高的结晶度。另外，钴基合金也可作为这种涂层材料的基材。