1) Cu-Mn complex oxides nanometer powder
纳米铜锰复合氧化物
1.
The grain growth kinetic index of Cu-Mn complex oxides nanometer powder precursor prepared by solid-solid state synthesis method is calculated and rules of grain growth is calcined.
通过对低热固-固化学反应法制备的纳米铜锰复合氧化物前驱物晶粒生长动力学的研究,得到其晶粒生长变化的规律,及晶粒生长激活能和动力学指数的平均值,分别是:E≈33。
2.
In this paper, the reaction precursors of Cu-Mn complex oxides nanometer powder were synthesized by solid-solid state synthesis method of the system with crystalline water and without crystalline water at room temperature, Technical conditions and the precursors kinetics were studied.
本文采用室温固-固相化学反应法,分别以含水乙酸盐和无水碳酸盐与草酸反应制备纳米铜锰复合氧化物,研究制备工艺条件及其优化;讨论前驱体的热分解过程动力学和晶粒生长动力学。
2) copper-manganese mixed oxide
铜锰复合氧化物
1.
Controlled Precipitation of Copper-Manganese Mixed Oxides for the Water Gas Shift Reaction;
铜锰复合氧化物变换催化剂的沉淀法可控合成
2.
The copper-manganese mixed oxides prepared by coprecipitation were tested for water gas shift reaction on a micro-reaction system with on-line GC analysis and characterized by XRD,TEM,BET and TPR.
国际知名的催化剂制造公司Topsφe在20世纪80年代首先研制成功了铜基宽温变换催化剂,并于1984年生产销售LK-811型铜锰复合氧化物高温变换催化剂,随后又报道了其改进型KK-142[5]。
4) nanocomposite
纳米复合氧化物
1.
Fe2O3-SnO2 nanocomposite oxide photocatalysts were prepared by the co-precipitation method.
用共沉淀法合成了Fe2O3-SnO2纳米复合氧化物光催化剂,并利用多种表征手段进行了表征。
5) nanocomposite oxide
纳米复合氧化物
1.
ZnO-SnO 2 nanocomposite oxide with Zn/Sn molar ratio of 2 was prepared by co-precipitation method.
采用共沉淀法合成了n(Zn) /n(Sn) =2的ZnO SnO2 纳米复合氧化物光催化剂 ,并采用X射线衍射 (XRD)、紫外 可见(UV Vis)漫反射吸收光谱、透射电子显微镜 (TEM)和N2 物理吸附等方法对在 5 0 0～ 130 0℃焙烧不同时间制得的ZnO SnO2纳米复合氧化物的物相组成、光吸收性能、晶粒尺寸、颗粒大小、比表面积和孔体积进行了表征 。
6) Fe-Mn-Cu Oxides
铁锰铜复合氧化物
补充资料：氧化亚锰
分子式：MnO
CAS号：
性质：又称氧化锰(manganese oxide)。灰绿色。立方晶系。密度5.43～5.46g/cm3。难溶于水，易溶于酸。长期存放于空气中被氧化。在低于1200℃，在氢气或氮气氛中焙烧碳酸锰而制得。用于制取各种锰化合物。
CAS号：
性质：又称氧化锰(manganese oxide)。灰绿色。立方晶系。密度5.43～5.46g/cm3。难溶于水，易溶于酸。长期存放于空气中被氧化。在低于1200℃，在氢气或氮气氛中焙烧碳酸锰而制得。用于制取各种锰化合物。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条