1) hyperbranched polymer
超支化高分子
1.
Reaction Dynamics and Statistics for A_aB_b Type Hyperbranched Polymers;
A_aB_b型超支化高分子的反应动力学和统计力学
2.
The molecule weight of the hyperbranched polymer was determined by GPC.
通过超支化单体中亚氨基和环氧基团之间的开环反应,得到了重均分子量为13900的超支化高分子。
3.
From the results, it is found that the properties of the terminal groups strongly affect the properties of the hyperbranched polymers.
对端羟基脂肪族超支化高分子的端基进行了乙酰化和硅烷化改性,研究了不同端基对超支化高分子的玻璃化温度,折光指数增量以及特性粘度的影响。
2) hyperbranched molecule
超支化分子
1.
0 G hyperbranched molecule was synthesized with methanol as solvent by means of Michael addition and amidation condensation reaction with octadecyl-amine,acrylate and ethylenediamine as raw materials.
0 G超支化分子;通过红外光谱、核磁共振手段对合成产品的结构进行了表征,且考察了十八烷基超支化分子对O/W型原油模拟乳液的破乳性能,并与传统的线性破乳剂SP-169进行了对比。
4) hyperbranched polymer
超支化大分子
1.
Advance on application of hyperbranched polymer;
超支化大分子的最新应用进展
5) supermolecular polymer chemistry
超分子高分子化学
1.
The basic concepts of supermolecular chemistry and supermolecular polymer chemistry were introduced.
简要介绍了超分子化学和超分子高分子化学的基本概念,并综述了其在油田化学领域的应用和发展前景。
6) high polymer supported catalyst
高分子支载催化剂
补充资料：高分子臭氧化
由臭氧引起的高分子化学反应。臭氧是化学活性极高的物质，较分子氧更容易与含有双键的高分子发生化学反应。大气中臭氧浓度虽然很低，但是，不饱和高分子遇臭氧易被氧化，产生与应力方向相垂直的裂纹，使高分子性能变坏。光能加剧臭氧化作用，故日光下的高分子化合物比黑暗中的更易臭氧化。
臭氧与不饱和高分子反应时，首先生成不稳定的臭氧化物（a），随后又重排为异臭氧化合物(b)。这种重排,可以发生链断裂,生成醛或酮，形成裂纹。高分子的臭氧化是严重的老化现象之一，可采用物理方法或化学方法防止（见橡皮龟裂）。
臭氧与不饱和高分子反应时，首先生成不稳定的臭氧化物（a），随后又重排为异臭氧化合物(b)。这种重排,可以发生链断裂,生成醛或酮，形成裂纹。高分子的臭氧化是严重的老化现象之一，可采用物理方法或化学方法防止（见橡皮龟裂）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。