1) belite
['bi:lait]
贝利特
1.
Advantages and Present Research of Belite Cement;
贝利特水泥的优势及研究现状
2.
Hydrating and hardening process of Belite-barium calcium sulpho-aluminate cement
贝利特-硫铝酸钡钙水泥的水化硬化过程
3.
Study on properties of belite-barium calcium sulphoaluminate cement
贝利特-硫铝酸钡钙水泥性能的试验研究
2) clinofibrate
克利贝特
3) high-belite
高贝利特
1.
It is an effective measure to produce high-belite cementitious material by burning gold mine tailings and limestone at high temperature after milling.
利用黄金尾矿和石灰石,通过配料、粉磨、高温煅烧制备出富含高贝利特相矿物的胶凝材料,实现黄金尾矿的资源化。
2.
Firstly, gold mine tailings was used to produce high-belite cement clinker.
本文在对黄金尾矿原料特性分析评价的基础上,结合水泥工业化生产的特点,对黄金尾矿煅烧制备高贝利特水泥熟料、利用高贝利特水泥熟料部分代替硅酸盐水泥作掺合料配制C80高性能混凝土以及将黄金尾矿用作大掺量水泥混合材的配方、工艺和性能进行了研究,力求提高黄金尾矿在水泥中的利用率、拓宽黄金尾矿的综合利用范围,降低水泥生产成本。
4) lifibrate
利贝特
5) Belite cement
贝利特水泥
1.
Belite cement gets attention because of its low energy consumption.
贝利特水泥由于能耗低而逐渐引起人们的关注。
2.
This paper suggests a method to clear away the toxicity of chromium-dregs by calcinating the mixture of flyash or coal gangue, limestone and chromium-dregs to produce a new type of Belite cement.
利用粉煤灰、石灰石、铬渣等为原料煅烧生产新型贝利特水泥可以去除铬渣毒性。
3.
The properties of belite cement which was prepared used tail were studied,and the composition of clinker and hydration production was analyzed by XRD and SEM in this paper.
本文以尾矿为主要原料制备了贝利特水泥并对其性能进行了研究,采用XRD和SEM对水泥通孰料的矿物和水化产物进行了分析。
6) High belite cement
高贝利特水泥
1.
Effect of fly ash on the workability,strength and hydration heat of high belite cement and concrete.;
粉煤灰对高贝利特水泥和混凝土的工作性、强度及水化热的影响
2.
This paper briefly introduces the production and the characteristic of high Belite cement, and discusses the main reason of its good workability, high long-term strength and perfect durability,meanwhile,also discusses its adaptability to the climate of Hainan.
简要介绍了高贝利特水泥的生产及其特性 ,讨论了高贝利特水泥具有工作性好、长期强度高和耐久性好的主要原因及其与海南气候的适应性 。
3.
Compatibility of high belite cement, Portland cement and ordinary Portland cement with superplasticizer and effect of mineral admixtures on the compatibility of high belite cement have been studied with the test of the workability of concrete as reaffirmation.
研究了高效减水剂与高贝利特水泥、硅酸盐水泥、普通硅酸盐水泥的相容性以及矿物掺合料对高贝利特水泥相容性的影响 ,并以混凝土工作性指标进行验证。
补充资料：贝利特
分子式：
CAS号：
性质：简称B矿。含有少量氧化铝、氧化铁、氧化钠、氧化镁、氧化钾等氧化物的硅酸二钙固溶体。有β、α′和α型。组成：氧化钙63.0%～63.7%，二氧化硅31.5%～33.7%，三氧化二铝1.1%～2.6%，三氧化二铁0.7%～2.2%；其余为氧化镁、氧化钠、氧化钾、二氧化钛、五氧化二磷等。二轴晶晶体折射率ng=1.735，nm=1.726，np=1.717，双折射率ng-np=0.018。硅酸盐水泥熟料中的重要矿物成分，但大多以β型存在于熟料。β型贝利特为单斜晶系，呈棱柱状或板状，在正常熟料中呈圆粒状，能使水泥石后期机械强度缓慢增长，并有抗硫酸盐侵蚀和水化热低的特点。
CAS号：
性质：简称B矿。含有少量氧化铝、氧化铁、氧化钠、氧化镁、氧化钾等氧化物的硅酸二钙固溶体。有β、α′和α型。组成：氧化钙63.0%～63.7%，二氧化硅31.5%～33.7%，三氧化二铝1.1%～2.6%，三氧化二铁0.7%～2.2%；其余为氧化镁、氧化钠、氧化钾、二氧化钛、五氧化二磷等。二轴晶晶体折射率ng=1.735，nm=1.726，np=1.717，双折射率ng-np=0.018。硅酸盐水泥熟料中的重要矿物成分，但大多以β型存在于熟料。β型贝利特为单斜晶系，呈棱柱状或板状，在正常熟料中呈圆粒状，能使水泥石后期机械强度缓慢增长，并有抗硫酸盐侵蚀和水化热低的特点。