1) long-term aging
长期时效
1.
Microstructures and high-temperature properties of a new Ni-based superalloy after long-term aging;
长期时效对一种新型镍基合金的组织及持久性能的影响
2.
Effects of long-term aging on microstructure and room-temperature tensile property of alloy GH4586B
长期时效对GH4586B合金组织及室温拉伸性能的影响
3.
The effects of long-term aging (800-900℃,(1-10)×l03 h) on the γ′ coarsening characteristics and the mechanical properties of a corrosion resistant Ni base superalloy K44 have been investigated.
研究了一种抗热腐蚀高温合金K44在800,850和900℃经(1-10)×103h长期时效后γ′相的变化和拉伸性能。
2) long term aging
长期时效
1.
The investigations of tensile properties of the second generation single crystal superalloy DD6 after long term aging at elevated temperature were presented.
研究了第二代单晶高温合金DD6长期时效后的拉伸性能。
2.
Microstructure character of γ′ precipitation and the corresponding thermodynamic calculation in superalloy Inconel 751 during long term aging treatment was studied.
对经过标准热处理的Inconel 751合金,在700℃和850℃进行了长期时效处理。
3.
The effect of long term aging at 950℃ for 500, 1000, 1500 and 2000 h on the microstructure and mechanical properties of alloy IC6 was investigated.
利用扫描电镜（SEM）、能谱（EDS）、透射电镜（TEM）等分析手段研究了IC6合金950℃长期时效500,1000,1500,2000h后的显微组织和力学性能。
3) long time aging
长期时效
1.
Microstructure after long time aging have been observed by means of SEM in GH169 alloys.
对GH169合金长期时效的组织结构观察表明,合金在650℃以下时效甚至长达5×10h,其组织变化并不明显,保持了良好的组织稳定性。
4) long term ageing
长期时效
1.
The effects of long term ageing to 1000h on microstructure and mechanical properties of superalloy GH783 at 750℃ were studied by testing mechanical properties and examing microstructure using optics microscope and SEM.
研究了750℃长期时效对GH783组织与性能的影响。
5) prolonged aging
长期时效
1.
By means of optical and TEM microstructure analyses,room temperature and 900 ℃ tensile tests and X-ray diffraction phase and microchemical quantitative analyses,the structure and mechanical property changes of GH4199 superalloy after prolonged aging in the temperature range of 600 ℃ to 900 ℃ and time period of 100 h to 1 000 h have been investigated.
采用金相和电镜微观组织观察、室温和高温拉伸试验、物理化学相分析等综合试验方法,对经600、700、800、900℃和100、200、5001、000 h长期时效处理的GH4199合金进行测试和研究。
2.
The effect of prolonged aging on the structures and properties of coblat base superalloy GH605 has been investigated.
研究了长期时效处理对钴基高温合金ＧＨ６０５组织与性能的影响。
6) long-term duration of time limit
长期时效期间
补充资料：《不适用法定时效公约》
《不适用法定时效公约》
Convention on the Non-Applicability of Statutory Limitations to War Crime and Crimes against Humanity
Bushiyong Fading ShixiQo Gongyue《不适用法定时效公约》(con、ntiono，lthe Nt，n确理lieabtlity ofstatu匆净Li从itationstow改rCrime韶dCri爪“ag，，i哪tHu从anily夕确保对犯有战争罪及危害人类罪的罪犯进行司法追究和惩办的国际条约。全称《战争罪及危害人类罪不适用法定时效公约》。1968年11月26日联合国大会通过，19祖年H月11日生效。至1975年4月，有苏联、印度、波兰等21国批准或加人。 公约包括序一言和11条正文。主要内容有:①战争罪及危害人类罪是国际法上最严重的罪行，是不1司于普通犯罪的国际罪，因此必须在国际法上确认此类罪行无时效期间之原则。②凡犯有1945年纽伦堡国际军事法庭组织法规定的，并经1946年联合国大会决议确认之战争罪和危害人类罪，不论其犯罪时间，任何法定时效均不适用。③公约的规定适用于以主犯或从犯身分参加或直接煽动他人犯上述罪行，或阴谋合伙犯上述罪行的国家当局代表及私人，及容许犯上述罪行之国家当局代表。④缔约国承允采取一切必要的国内立法或其他措施，以确保法定或他种时效不适用于对犯有本公约所指各该罪的追诉权及行刑权;倘有此项时效规定，应予废止;缔约国还应采取措施，为引渡犯有公约所指各罪之人创造条件。 该公约是针对曾经发动第二次世界大战的国家欲使法定时效用于战犯而制定的。公约的缔结标志着国际法中业已形成的战争罪和危害人类罪不适用法定时效的原则以法律形式固定下来，对那些企图以各种借口停止对战犯追究的国家当局有一定约束。但是，由于一些国家对战犯的包庇、纵容，公约有关规定未能认真执行，德国、日本的许多第二次世界大战重要战犯未受到应有惩处。 (王可菊王洪钓)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条