1) Intercritical Annealing
两相区退火
1.
This paper studies the effects of silicon content and intercritical annealing conditions on retained austenite and mechanical properties of the two low-carbon cold-rolled TRIP steels,which containing silicon content 1.
研究了硅含量分别为 1 5wt%和 1 0wt %的冷轧低碳硅锰TRIP钢两相区退火温度对残留奥氏体量和力学性能的影响。
2) tercritical annealing temperature
两相区退火温度
1.
5Mn冷轧TRIP钢两相区退火温度对组织和力学性能的影响,结果表明,试验钢经780℃退火5 min和400℃等温5min处理后可以获得10％的残余奥氏体,较低或较高的退火温度都将使残余奥氏体量略微下降。
3) intercritical annealing
双相区球化退火
1.
The intercritical annealing process of 50Cr alloy steel wire with plastic deformation was probed into with the method of orthogonal test for the better result of spheroidal annealing with the oven free of oxygen in the process of metatic card clothing wire production.
为了金属针布钢丝制造企业在球化退火过程中利用无氧化罩式炉更好地保证球化效果,采用正交试验法,对塑性变形50Cr合金钢丝进行双相区球化退火工艺研究。
2.
One was the conventional intercritical annealing.
采用常规双相区球化退火和亚温球化退火工艺研究了常规轧制(CR)和控轧控冷(CRC)的中碳钢SWRCH35K的球化退火行为和力学性能。
3.
The intercritical annealing process of 70Nb alloy steel wire with severe plastic deformation is studied by using orthogonal test method.
采用正交试验法研究了大塑性变形70Nb合金钢丝双相区球化退火工艺。
4) two steps annealing
两步退火
1.
Mg-gradual-δ-doping in GaN epilayers and two steps annealing method to active Mg have been investigated by metalorganic chemical vapor deposition.
采用MOCVD技术及渐变-δMg掺杂方法生长了p型GaN薄膜,对样品进行了两步退火处理以对Mg进行激活。
5) second stage annealing
两段退火
6) two-stage annealing
两阶段退火
1.
The influences of variant heat treatment processes(two-stage annealing and solution strengthening) on the mechanical properties and the microstructure of TC18 titanium alloy large forgings were investigated through detections of mechanical properties as well as microstructure & XRD phase analyses.
采用两阶段退火和固溶强化两种典型的热处理制度,通过力学性能检测、显微组织分析和XRD物相分析,系统研究了整体热处理工艺对TC18钛合金大型锻件组织和性能的影响。
补充资料：软化退火(见低温退火)
软化退火(见低温退火)
soft-annealing
rU0nhUO tUihUO软化退火(soft一annealing)见低温退火。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。