1) resistance against sulfide stress cracking
抗硫化物应力开裂
2) resistance to SSC test
抗硫化物应力开裂试验
3) SSCC
硫化物应力腐蚀开裂
1.
Constant load tensile test was adopted to study the influence of welding material match and alloy element content on SSCC(sulfide stress corrosion cracking) of domestic pipeline steels.
采用恒载荷拉伸法,测试了国产管线钢母材及其焊接接头的硫化物应力腐蚀开裂SSCC性能。
4) sulfide stress corrosion cracking
硫化物应力腐蚀开裂
1.
In order to prevent pipeline steels from more loss in advance of cracking, the study on sulfide stress corrosion cracking (SSCC) properties for domestic X70 pipeline steels became more and more important.
随着国产X70管线钢在西气东输工程中的应用,国产高强度管线钢硫化物应力腐蚀开裂(SSCC)性能研究显得尤为重要。
5) sulfide stress corrosion cracking(SSCC)
硫化物应力腐蚀开裂
1.
Using the NACE standard bent-beam test,sulfide stress corrosion cracking(SSCC) of different types microstructure in X70 grade pipeline steel with different types of microstructure was investigated.
用三点弯曲方法及SEM、TEM等手段研究了不同组织类型的X70级管线钢硫化物应力腐蚀开裂(SSCC)行为。
6) sulfide stress corrosion cracking (SSC)
硫化物应力腐蚀开裂(SSC)
1.
The research status of low Crcorrosion resistant casing and tubing as well as gathering line materials is reviewed in this paper, and the anti-CO2/H2S uniform and local corrosion and sulfide stress corrosion cracking (SSC) ability of low Cr steel are introduced in detail.
综述了国内外低Cr耐蚀油套管、集输管线材料的研究现状,详细介绍了低Cr钢抗CO2/H2S均匀腐蚀、局部腐蚀和硫化物应力腐蚀开裂(SSC)的性能及影响因素,同时介绍了低Cr钢对缓蚀剂缓蚀效率的影响及使用的经济性,指出了国内研制开发的低Cr耐蚀管材与国外的差距及需要采取的措施,并展望了其在国内油气田的应用前景及发展方向。
补充资料：硫化物还原
分子式：
CAS号：
性质：以硫化物为还原剂对芳香族硝基化合物作用使之转换为胺类化合物的过程。常用的硫化物为硫化钠、硫氢化钠、多硫化钠。在某些情况下，硫化铵、硫氢化铵、硫化锰、硫化铁也可以用作还原剂。用硫化物还原，反应进行得比较温和，可使多硝基化合物中的硝基选择性地部分还原，或只还原硝基偶氮苯化合物中的硝基，而保留偶氮基。对酸敏感的硝基化合物，不宜用铁粉还原时，可应用硫化物在碱性介质中还原。
CAS号：
性质：以硫化物为还原剂对芳香族硝基化合物作用使之转换为胺类化合物的过程。常用的硫化物为硫化钠、硫氢化钠、多硫化钠。在某些情况下，硫化铵、硫氢化铵、硫化锰、硫化铁也可以用作还原剂。用硫化物还原，反应进行得比较温和，可使多硝基化合物中的硝基选择性地部分还原，或只还原硝基偶氮苯化合物中的硝基，而保留偶氮基。对酸敏感的硝基化合物，不宜用铁粉还原时，可应用硫化物在碱性介质中还原。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条