1) sulfide stress corrosion cracking
硫化氢应力腐蚀开裂
1.
Accordingly, the accident of sulfide stress corrosion cracking (SSCC) should be taken into account.
针对制造过程中由于开孔失误而进行补焊的冷高压分离器在高压、高浓度的H2S环境的使用安全问题,采用了电化学充氢、恒应变和慢拉伸的实验方法,研究了制造冷高压分离器的主体材料16Mn(HIC)钢和普通的16Mn钢及其焊缝的氢扩散系数,在不同H2S浓度、pH值,模拟冷高压分离器操作环境溶液和实际溶液中的腐蚀规律和硫化氢应力腐蚀开裂(SSCC)敏感性,结合实际腐蚀环境的检测和分析结果,对补焊后的冷高压分离器的使用安全给出了综合评估。
2) Sulfide stress corrosion crack
氢致开裂硫化物应力腐蚀开裂
3) corrosion crack caused by hydrogen sulphide
硫化氢腐蚀开裂
4) SSCC
硫化物应力腐蚀开裂
1.
Constant load tensile test was adopted to study the influence of welding material match and alloy element content on SSCC(sulfide stress corrosion cracking) of domestic pipeline steels.
采用恒载荷拉伸法,测试了国产管线钢母材及其焊接接头的硫化物应力腐蚀开裂SSCC性能。
5) sulfide stress corrosion cracking
硫化物应力腐蚀开裂
1.
In order to prevent pipeline steels from more loss in advance of cracking, the study on sulfide stress corrosion cracking (SSCC) properties for domestic X70 pipeline steels became more and more important.
随着国产X70管线钢在西气东输工程中的应用,国产高强度管线钢硫化物应力腐蚀开裂(SSCC)性能研究显得尤为重要。
6) sulfide stress corrosion cracking(SSCC)
硫化物应力腐蚀开裂
1.
Using the NACE standard bent-beam test,sulfide stress corrosion cracking(SSCC) of different types microstructure in X70 grade pipeline steel with different types of microstructure was investigated.
用三点弯曲方法及SEM、TEM等手段研究了不同组织类型的X70级管线钢硫化物应力腐蚀开裂(SSCC)行为。
补充资料：纯硫化氢
分子式： H2S
CAS号：
性质：纯度99.9%。在常温常压下为臭鸡蛋味的无色有毒气体。易燃，能与空气混合形成爆炸性气体，易溶于水。空气中的爆炸界限为4.0%～44.0%。纯硫化氢可由电解氢和硫磺直接合成，经纯化而成。用于半导体生产、化学分析、金属精制等。也可用作有机合成的还原剂、标准气、校正气。
CAS号：
性质：纯度99.9%。在常温常压下为臭鸡蛋味的无色有毒气体。易燃，能与空气混合形成爆炸性气体，易溶于水。空气中的爆炸界限为4.0%～44.0%。纯硫化氢可由电解氢和硫磺直接合成，经纯化而成。用于半导体生产、化学分析、金属精制等。也可用作有机合成的还原剂、标准气、校正气。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条