1) single-pod ZnO
单针状氧化锌
1.
The antistatic result of the aqueous emulsion suspended with single-pod ZnO whiskers are better than that of the aqueous emulsion suspended with tetrapod ZnO whiskers.
实验结果表明:悬浮有单针状氧化锌晶须的乳液其抗静电效果优于悬浮有四针状氧化锌晶须的乳液;当聚丙烯腈初生纤维在悬浮有单针状氧化锌晶须的乳液中停留时间为20 s时,聚丙烯腈纤维体积比电阻率降为4。
3) multipod-like ZnO
多针状氧化锌
1.
850 ～ 950 ℃,oxygen partial pressure ≤8%,and total gas flow rate 300 ～ 330 L/h,multipod-like ZnO powders were directly prepared by vapor phase oxidizing zinc powders.
采用气相氧化法,在温度850～950℃,氧分压≤8%,气体总流量300～330 L/h的条件下,用工业锌粉为原料直接氧化制备出多针状氧化锌。
4) nano-sized needle-shape zinc oxide
纳米针状氧化锌
5) tetrapod-shaped ZnO
四针状氧化锌
1.
Dispersing the Tetrapod-Shaped ZnO whisker pre-treated with vinyltrimethoxysilane in Polyacrylonitrile film and By the means of adding different contents of tetrapod-shaped ZnO whisker into the Polyacrylonitrile(PAN) films, it is found that the specific volume resistivity of the films decrease rapidly with the increasing of the Tetrapod-Shaped ZnO whisker content.
将用硅烷偶联剂处理的四针状氧化锌晶须分散在聚丙烯腈薄膜中,测试薄膜的体积比电阻率,发现3%(相对于聚丙烯腈干粉质量分数)便可以起到良好的抗静电作用。
6) T-ZnOw
四针状氧化锌晶须
1.
The tetrapod-like zinc oxide whisker (T-ZnOw) is the sole tetrapod-like whisker in crystal whisker family, which has clear and neat three-dimensional space structure.
四针状氧化锌晶须 (T -ZnOw)是晶须家族中目前发现的唯一具有规整三维空间结构的四针状晶须。
2.
The surface of tetra-needle like zinc oxide whisker(T-ZnOw) was modified by silane coupling agent(KH-560) and titanate coupling agent(TM-38S).
采用硅烷偶联剂KH-560和钛酸酯偶联剂TM-38S对四针状氧化锌晶须(T-ZnOw)进行表面改性,制备了相应的聚苯硫醚(PPS)尼/龙(PA)66/T-ZnOw复合材料,研究了两种偶联剂及其复合体系对T-ZnOw表面改性效果和相应复合材料力学性能的影响,并利用扫描电子显微镜对复合材料的断面形态进行了观察。
3.
The microwave depleting mechanisms of tetra-needle like zinc oxides (T-ZnOw) have been discussed.
分析了四针状氧化锌晶须(T-ZnOw)的电磁波损耗机理,首先从T-ZnOw形成立体导电网及其感应涡流损耗和晶须内部散射电场计算等宏观角度讨论了入射电磁波损耗机制;其次,从针尖电荷集中和界面极化的角度分析了该晶须的电磁波损耗机理;最后,用量子力学的观点讨论了T-ZnOw与电磁波作用机理,发现隧道效应和量子势阱理论都可用于解释该晶须在2-18 GHz频率范围内的电磁波损耗。