1) harden time
硬化时间
1.
The experimental study on harden time of silica sol shell molding with 15%NH4Cl and subnano-SiO2 was run in this paper.
对添加15%NH4Cl和亚纳米SiO2的硅溶胶型壳硬化时间进行试验研究。
2.
The experimental study on harden time of silica sol sh ell molding with 15%NH4Cl and subnano-SiO2 was run in this paper.
本文对添加15%NH4Cl和亚纳米SiO2的硅溶胶壳型硬化时间进行试验研究。
3.
It is found that the coagulation harden time of the FS-Ⅱquick-dry silica sol shell is 3 h;the JN-30 silica sol shell is 12 h.
实验研究发现:控制环境温度(22±2)℃、相对湿度50%～60%和风速4～6 m/s时,FS-Ⅱ型快干硅溶胶型壳的胶凝硬化时间为3 h,而JN-30硅溶胶型壳为12 h。
3) time hardening
时间硬化
1.
By comparing typical temperature deformation accumulation models,and on the basis of time hardening superposition approach,a new superpos.
通过典型温度变形叠加方法的比选,在时间硬化叠加方法的基础上,建立了变温下沥青混合料剪切疲劳变形的叠加模型。
4) setting-up period
固化(或硬化)时间
6) gel-hardening time
胶凝硬化时间
1.
The results show that the gel-hardening time of the ceramic mold production was about 8 minutes, and a high wet strength of 0.
8、18%、10%的条件下,所生产的陶瓷铸型的胶凝硬化时间为8min左右,湿强度为0。