1) time hardness
时间硬度
2) time-temperature-hardness curve
时间-温度-硬度曲线
1.
The quench sensitivity of 7055 aluminum alloy was studied with time-temperature-hardness curve evaluated via interrupted quenching and transmission electron microscopy.
通过测定时间-温度-硬度曲线并采用透射电镜研究7055铝合金的淬火敏感性。
3) harden time
硬化时间
1.
The experimental study on harden time of silica sol shell molding with 15%NH4Cl and subnano-SiO2 was run in this paper.
对添加15%NH4Cl和亚纳米SiO2的硅溶胶型壳硬化时间进行试验研究。
2.
The experimental study on harden time of silica sol sh ell molding with 15%NH4Cl and subnano-SiO2 was run in this paper.
本文对添加15%NH4Cl和亚纳米SiO2的硅溶胶壳型硬化时间进行试验研究。
3.
It is found that the coagulation harden time of the FS-Ⅱquick-dry silica sol shell is 3 h;the JN-30 silica sol shell is 12 h.
实验研究发现:控制环境温度(22±2)℃、相对湿度50%～60%和风速4～6 m/s时,FS-Ⅱ型快干硅溶胶型壳的胶凝硬化时间为3 h,而JN-30硅溶胶型壳为12 h。
4) time hardening
时间硬化
1.
By comparing typical temperature deformation accumulation models,and on the basis of time hardening superposition approach,a new superpos.
通过典型温度变形叠加方法的比选,在时间硬化叠加方法的基础上,建立了变温下沥青混合料剪切疲劳变形的叠加模型。
5) hard time window
硬时间窗
1.
Research on heterogeneous vehicle routing problem with hard time windows for the third party logistics;
第三方物流多车型硬时间窗路线问题研究
6) firm time
变硬时间
补充资料：老化温度-时间曲线
分子式：
CAS号：
性质：用以求取高分子材料的耐热老化寿命。老化寿命τ值与温度间有如下关系:lnτ=ΔE/RT+B式中，ΔE为反应活化能；T为热力学温度；R为气体常数；B为常数。通过几个温度点做实验，获得各温度点在老化过程中，有关性能变化与时间关系的动力学曲线图。由此求出各温度点达到特定老化状态时的时间，即寿命值τ。
CAS号：
性质：用以求取高分子材料的耐热老化寿命。老化寿命τ值与温度间有如下关系:lnτ=ΔE/RT+B式中，ΔE为反应活化能；T为热力学温度；R为气体常数；B为常数。通过几个温度点做实验，获得各温度点在老化过程中，有关性能变化与时间关系的动力学曲线图。由此求出各温度点达到特定老化状态时的时间，即寿命值τ。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。