1) Curie point
Curie点
1.
The influence of Cu concentration x(x=3,5,8) on the martensitic transformation temperature and Curie point of Co41Ni33Al26 alloys were investigated by optical Metallography,DSC and VSM methods.
采用金相显微技术、DSC、VSM方法,研究了Cu含量x(x=3,5,8)对Co41Ni33Al26合金马氏体相变和Curie点的影响。
2.
It is found that the martensitic transformation temperatures and Curie points of Co_(40)Ni_(33.
5合金马氏体相变和Curie点随淬火温度变化的情况,结果发现该合金马氏体相变温度和Curie点与淬火温度成正比关系。
3.
The influence of cobalt concentration x on martensitic transformation temperature and Curie point of Ni_(54)Al_(25)Fe_(21-x)Co_x alloys were investigated by optical micrography,SEM,DSC and VSM and EDX analysis.
淬火温度降低会显著降低Ni54Al25Fe21-xCox合金的马氏体相变温度和Curie点Tc,但随着x的提高,淬火温度对马氏体相变温度和Tc的影响程度减小。
2) Curie temperature
Curie温度
1.
The superfluous Mn and Fe can reduce the Curie temperature from 343 K to 294 and 286 K, respectively.
过量的Mn和Fe都会使合金的Curie温度降低,由343K(化学计量比)降低到294K(过量Mn)和286K(过量Fe);过量的Mn能减小热滞,而过量的Fe会使热滞增加;磁熵变也有所减小,在1。
2.
The factors influencing the Curie temperature of piezoelectric ceramics are summarized as well.
总结了影响压电陶瓷Curie温度的影响因素。
3.
The enhancement of Curie temperature of the intergranular amorphous phase in duplex-phase alloy Fe73.
5B9合金的纳米晶粒大小、纳米晶相所占体积分数以及晶间非晶相厚度对晶间非晶相Curie温度的影响。
3) Curie temperature(T_c)
Curie温度(Tc)
4) the formula of Curie-Weiss
Curie-Weiss公式
5) curie temperature T c
Curie温度Tc
6) extrapolation Curie temperature
居里-外斯温度(Curie-Weiss temperature)