1) Rheoforming
流变成形
1.
Research Progress on Rheoforming Technology of Semi-solid Alloy;
半固态合金流变成形技术的研究进展
2.
Experimental Study on Twin-roll Strip Rheoforming for Semi-solid Magnesium Alloy;
镁合金半固态双辊板带流变成形研究
3.
Developing Tendency and Countermeasures of Rheoforming Slurry-making;
流变成形浆料制备技术发展动向及其对策
3) Rheological Forming
流变成形
1.
Failure and Material Selection of the Mold Used for Ferrous Metal in Semi-solid Rheological Forming;
半固态金属流变成形模具失效与选材
2.
The theory of rheological forming, a deformation theory of greater universal significance, has been developed recent years based on the theories of plastic forming, superplastic forming and creep forming.
流变成形理论是近年来在塑性成形原理、超塑性成形、蠕变成形理论的基础上发展起来的、更富普遍性意义的一种成形理论，是流变学在塑性加工领域的具体应用。
5) thermal-rheological forming
热流变成形
1.
Contrapositive to the quality problems appearing in the process of the thermal-rheological forming production of TC1 titanium alloy rectifier , such as the failure phenomenon of drawing splitting, wrinkling,etc.
对TC1钛合金整流内罩在深拉热流变成形生产过程中出现的质量问题 ,如拉裂、起皱等失效现象 ,采用数值模拟方法加以质量控制研究 。
2.
In this paper, the FE numerical simulation of the thermal-rheological forming of aluminum alloy (Lc4)part (shown in Fig.
介绍铝合金(Lc4)零件热流变成形的有限元数值模拟。
6) Semi-solid Rheoforming
半固态流变成形
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。