1) cold upsetting deformation
冷压形变
2) cold-press forming
冷压成形
1.
According manufacture difficult of small special-shaped punch in die manufacturing,introduced cold-press forming(three-dimensional press),it provided a certain reference for manufacture of similar small special-shaped punchs.
针对模具制造中遇到的微小异形凸模难加工问题,介绍了采用冷压成形工艺——立体压制方法。
3) cold-drawing deformation
冷拉形变
1.
The compound strengthening and toughening of sub-critical quenching and cold-drawing deformation on 20CrMnMo steel was studied.
对20CrMnMo进行亚温淬火热处理和冷拉形变的复合强韧化研究。
4) cold deformation
冷变形
1.
Investigation on cold deformation and dynamic recrystallization of Cu-Ni-Si-Ag alloy;
Cu-Ni-Si-Ag合金冷变形及动态再结晶研究
2.
Effect of cold deformation and tempering on ductility of low carbon martensite steel;
冷变形低碳马氏体钢的回火塑性
3.
Effects of Cold Deformation on Super-elasticity and Microstructure of TiNiCr Shape Memory Alloys;
冷变形对TiNiCr形状记忆合金超弹性和组织的影响
5) cold rolling
冷轧变形
1.
The effect of cold rolling deformation prior to aging on the strengthening of a maraging steel was investigated.
系统研究了预先冷轧变形对马氏体时效钢强化的影响,研究结果表明:510℃×3 h时效引起的强度净增加值恒定,与冷轧变形量无关,最终的强度为:σ=σ0+ΔσCR+ΔσAge,即初始强度、冷加工强化和时效强化的叠加,其中只有冷加工强化ΔσCR随变形量变化。
2.
The article introduces microstructure evolution and mechanical hardening of three different kind steels during cold rolling.
本文介绍了三种钢在冷轧变形过程中的组织演变和形变强化规律，发现三种钢具有不同的形变强化规律。
6) deformation during cooling
冷却变形
补充资料：冷压焊
在常温下只靠外加压力使金属产生强烈塑性变形而形成接头的焊接方法。加压变形时，工件接触面的氧化膜被破坏并被挤出，能净化焊接接头。所加压力一般要高于材料的屈服强度，以产生60～90％的变形量。加压方式可以缓慢挤压、滚压或加冲击力，也可以分几次加压达到所需的变形量。冷压焊的工件一般是塑性金属,如铝、铜、镉、镍和银等。冷压焊有搭接点焊和对接焊两种。搭接点焊前工件表面须经机械加工,或用钢丝刷(轮)或溶剂仔细清理，对接焊时表面清理要求不太严格。冷压焊设备只需一台挤压机，包括压膜和夹持钳口，也可用手动夹具焊接小工件。冷压焊时工件不必加热，因而适于焊接不允许有温升的工件和加热时会引起软化的材料，也适用于易产生脆性化合物的异种金属连接。冷压焊已应用于电容器外壳的封装、电气工业中铝铜过渡接头、导电母线、引出线、铝制日用品和包装带的焊接等。铝与铝对接可焊截面达1500毫米2,铝与铜对接可焊截面达1000毫米2。冷压焊所需设备简单，工艺简便,劳动条件好。但冷压焊所需挤压力较大，在大截面工件的焊接时设备较庞大，搭接焊后工件表面有较深的压坑，因而在一定程度上限制了它的应用范围。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。