1) copolymerization emulsion of PVC seeds and acrylates
PVC种子/丙烯酸酯共聚乳液
1.
Influences of copolymerization emulsion of PVC seeds and acrylates on the impact properties of PVC resins;
PVC种子/丙烯酸酯共聚乳液对PVC冲击性能的影响
2) acrylic copolymerized ed latex
丙烯酸酯共聚种子乳胶
3) acrylate copolymer emulsion
丙烯酸酯共聚乳液
1.
The main component is acrylate copolymer emulsion with core-shell structure, which is synthesized by seeded emulsion co-polymerization.
介绍了印刷纸张用水性上光剂的配制,主剂为采用种子乳液聚合法合成的具有核-壳结构的丙烯酸酯共聚乳液。
2.
Acrylate copolymer emulsion adhesive is one of the important applications for emulsion polymerization.
本课题针对丙烯酸酯共聚乳液胶粘剂的研究现状,根据分子设计原理进行乳液共聚合,优化合成工艺,调整配方组合,制备出多元共聚型丙烯酸酯乳液,并实践应用于纸塑复膜胶粘剂与汽车内饰胶粘剂。
4) acryate copolymeric emulsion
丙烯酸酯类共聚物乳液
6) Acrylic copolymer latex
丙烯酸酯共聚物乳液
1.
Acrylic copolymer latexes(PA) and waterborne polyurethane(PU) have been widely used as the film-forming materials of waterborne coatings,and both of them have their own characteristic advantages and disadvantages.
本论文制备了丙烯酸酯共聚物乳液,主要探讨了不同的制备方法、软硬单体(甲基丙烯酸甲酯MMA、苯乙烯St、丙烯酸丁酯BA)的用量、双丙酮丙烯酰胺(DAAM)的用量、种子乳液用量、丙烯腈单体(AN)的用量、以及乳化剂COPS-I与CO-436配比等因素对乳液和乳胶膜性能的影响。
补充资料：PVC
结构式【－CH2-CHCl]n-
由单体氯乙烯经加聚反应生成的热塑性线型树脂。工业品为白色或浅黄色粉末。密度（20/4℃）1.40g/cm3，含氯量56～58％。低分子量的易溶于酮类，酯类和氯代烃类等溶剂。高分子量的难溶。聚氯乙烯树脂经加工成型就得到聚氯乙烯塑料。其单体成本低、生产工艺成熟、易加工成型。耐酸碱性、耐磨性、电绝缘性好，不燃烧；但热稳定性和耐光性差。140℃分解放出氯化氢，在加工成型过程中，需加入稳定剂。软化温度低，限在80℃以下使用。根据所加增塑剂的多少，可制得软质塑料和硬质树脂。软质塑料可用作电线电缆包皮和其它绝缘材料，可制成透明薄膜，用作雨衣、台布、农用育秧薄膜等；还用来制人造革、泡沫塑料和氯纶纤维。硬质塑料可用于制板材、管道、贮槽、吸收塔等。氯乙烯经悬浮法聚合可得粉末状树脂，若用乳液法聚合，可得糊状树脂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。