1) PU/PA copolymer emulsions
聚氨酯/丙烯酸酯共聚乳液
2) polyurethane-acrylate emulsion
聚氨酯丙烯酸酯乳液
1.
The UV-curable waterborne polyurethane-acrylate emulsion modified by epoxy resin was prepared with toluenediisocyanate(TDI-80) ,polyether(N220) ,dimethylolpropionic acid(DMPA) ,1,4-butanediol(BDO) ,epoxy resin and hydroxypropyl acrylate(HPA) as the main materials.
结果表明,通过加入适量的环氧树脂,聚氨酯丙烯酸酯乳液的稳定性和耐水性得到明显改善,当二羟甲基丙酸用量为6%左右、环氧树脂用量为4%～8%、中和度为90%～95%时,所得到的聚氨酯丙烯酸酯聚合物乳液的外观和稳定性较好。
3) acrylate copolymer emulsion
丙烯酸酯共聚乳液
1.
The main component is acrylate copolymer emulsion with core-shell structure, which is synthesized by seeded emulsion co-polymerization.
介绍了印刷纸张用水性上光剂的配制,主剂为采用种子乳液聚合法合成的具有核-壳结构的丙烯酸酯共聚乳液。
2.
Acrylate copolymer emulsion adhesive is one of the important applications for emulsion polymerization.
本课题针对丙烯酸酯共聚乳液胶粘剂的研究现状,根据分子设计原理进行乳液共聚合,优化合成工艺,调整配方组合,制备出多元共聚型丙烯酸酯乳液,并实践应用于纸塑复膜胶粘剂与汽车内饰胶粘剂。
4) acryate copolymeric emulsion
丙烯酸酯类共聚物乳液
6) Acrylic copolymer latex
丙烯酸酯共聚物乳液
1.
Acrylic copolymer latexes(PA) and waterborne polyurethane(PU) have been widely used as the film-forming materials of waterborne coatings,and both of them have their own characteristic advantages and disadvantages.
本论文制备了丙烯酸酯共聚物乳液,主要探讨了不同的制备方法、软硬单体(甲基丙烯酸甲酯MMA、苯乙烯St、丙烯酸丁酯BA)的用量、双丙酮丙烯酰胺(DAAM)的用量、种子乳液用量、丙烯腈单体(AN)的用量、以及乳化剂COPS-I与CO-436配比等因素对乳液和乳胶膜性能的影响。
补充资料：甲基丙烯酸甲酯-丙烯酸乙酯-丙烯酸甲酯共聚物
分子式：
CAS号：
性质：甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸甲酯三元热塑性共聚物。在本体或悬浮聚合中，适量加入丙烯酸乙酯或丙烯酸甲酯或两者，可改进聚甲基丙烯酸甲酯的柔韧性和流动性。如甲基丙烯酸甲酯和少量丙烯酸酯(甲酯、乙酯)由悬浮聚合制得的模塑料，视丙烯酸酯的品种和加量不同，有的可作挤塑板用，有的可作PVC改性剂等。在溶液和乳液聚合中，甲基丙烯酸甲酯为“硬单体”，丙烯酸甲酯、丙烯酸乙酯为“软单体”，适当调节它们的比例，可制得成膜软硬度不同的液状树脂。适用于作涂料、漆料、织物和皮革处理剂等。
CAS号：
性质：甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸甲酯三元热塑性共聚物。在本体或悬浮聚合中，适量加入丙烯酸乙酯或丙烯酸甲酯或两者，可改进聚甲基丙烯酸甲酯的柔韧性和流动性。如甲基丙烯酸甲酯和少量丙烯酸酯(甲酯、乙酯)由悬浮聚合制得的模塑料，视丙烯酸酯的品种和加量不同，有的可作挤塑板用，有的可作PVC改性剂等。在溶液和乳液聚合中，甲基丙烯酸甲酯为“硬单体”，丙烯酸甲酯、丙烯酸乙酯为“软单体”，适当调节它们的比例，可制得成膜软硬度不同的液状树脂。适用于作涂料、漆料、织物和皮革处理剂等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。