1) precipitate-free zone
无析出物区
1.
20 mm thick 2519-T87 high strength aluminum alloy was surfacing welded,and a precipitate-free zone (PFZ) was found behind the grain boundary in partially melted zone (PMZ).
采用电弧焊对20mm厚的2519-T87高强铝合金进行表面堆焊,观察了部分熔化区出现的无析出物区(PFZ)的组织特征,并对该区域的形成机理进行了研究。
2) precipitate free zone
无析出区
1.
Effect of precipitate free zone quench-induced on fracture behavior of Al-Zn-Mg-Cu alloys;
淬火无析出区对Al-Zn-Mg-Cu合金断裂行为的影响
3) burnt deposit
无光泽析出物
4) Non-blooming
无析出
1.
Effect of Nano-material as a Nucleating Agent on the Crystallization Rate of Polyethylene Terephthalate and Application of Non-blooming Flame Retardant on Glass Fiber Reinforced Polyethylene Terephthalate、Polybutylene Terephthalate Composites;
然后本文研究一种低分子无析出阻燃剂A和十溴联苯醚对玻纤增强工程塑料体系综合性能的影响。
5) sludge analysis
析出物分析
6) precipitates
[英][pri'sipitit] [美][prɪ'sɪpətɪt]
析出物
1.
Effect of Deforming Temperature on Structure and Precipitates of 0.05C-0.13Nb Steel;
变形温度对0.05C-0.13Nb钢组织和析出物的影响
2.
The mechanical property of steel Q345B at elevated temperature is tested and the type of the precipitates existing at the cracks is identified and thereupon cause to formation of the corner cracks is analyzed and the processing measures to eliminate the defect accordingly is put forward.
测试了Q345B钢的高温力学性能,鉴别了铸坯裂纹处析出物的类型,在此基础上分析了连铸坯角裂形成原因,并提出了消除角裂的工艺措施。
3.
The precipitates in hot rolled strip of two grades of non-oriented electrical steel(W540,W800) produced by CSP process and one grade of non-oriented electrical steel(W20) produced by conventional process were investigated.
对CSP流程生产的W540和W800两个牌号的无取向电工钢热轧板中析出物尺寸在卷取前后的变化进行了研究,并和传统流程生产的W20热轧板的析出物进行了比较。