1) ceramic mold
陶瓷型
1.
Application of Phosphate Bonding Agent to Art Casting in Ceramic Mold;
磷酸盐粘结剂用于陶瓷型艺术铸造
2.
Molding Practice for the Thousandth Auspicious Bell with 21t weight in Wuhan-Introduction for a New Craft of Coating and Laying Sand Pulp Ceramic Mold;
武汉21t千年吉祥钟的造型实践——涂敷浆砂陶瓷型新工艺
3.
Dry stock of silica sol ceramic mold was prepared by the colloidal molding technique and optimized vacuum drying process.
采用胶态成型技术和优化的真空干燥工艺制备硅溶胶陶瓷型干坯料,并探讨焙烧工艺对其收缩率和抗压强度的影响。
2) ceramic mould
陶瓷型
1.
In this paper, ceramic mould is used to produce small and medium-sized magnesium moulds by gravity casting and low-pressure casing respectively.
本文采用SiO2陶瓷型,利用重力铸造和低压铸造方法制造了中、小型的镁合金模具。
2.
Manufacture of magnesium alloy castings by ceramic mould can not only shorten the production cycle, boost the production efficiency, but also produce parts with required precision with no or less machining which can lower the production cost.
大型、表面形状复杂的镁合金制件大多需要在铸件基础上进行机加工,采用陶瓷型铸造镁合金铸件,不仅缩短生产周期,提高生产效率,且能在少无切削条件下生产出合乎精度要求的制件,从而降低生产成本。
3) ceramic core
陶瓷型芯
1.
Quality evaluation of the ceramic core shaped by side extrusion and mould design;
侧向挤压陶瓷型芯模具设计与型芯质量评估
2.
Effects of Na_2O Content in Filler on Quality of Ceramic Core;
填料中Na_2O含量对陶瓷型芯质量的影响
4) new-type ceramics
新型陶瓷
1.
This paper introduces basic concept and new sintering principle of new-type ce- ramics materials,and conducts analyse and study to property of new-type ceramics,the study indi- cated that it is feasible that the new-type ceramics which are used to design and manufacture io- dine salt packer mechanical spares replace metal materials.
文章介绍了新型陶瓷材料的基本概念和新的烧结原理,对新型陶瓷的性能进行了分析研究。
5) Ceramic shell
陶瓷型壳
1.
Face and back coating materials of ceramic shells were analysed by TG-DTA and X ray diffraction.
通过TG -DTA、X衍射对氧化物陶瓷型壳的面层和背层进行了分析 ,测试了陶瓷型壳的常温、高温力学性能和热膨胀系数 ,对型壳试样的断口进行了SEM观察 。
2.
Employing different proportion of mineralizer and different concentration of silica sol,the ceramic shells were prepared.
采用不同比例矿化剂用量及不同浓度的硅溶胶配制涂料,按照一定工艺制得陶瓷型壳试样,研究了涂料的流变性能,型壳的力学性能及其高温抗蠕变性能。
6) ceramic shell mold
陶瓷型壳
1.
The ceramic shell mold of precision casting titanium and Ti-alloy is made from slurry by sinter, and the slurry is prepared by blending refractory materials with bond.
钛和钛合金的熔模精铸陶瓷型壳是以化学方式将粘结剂与耐火材料混合制成涂料浆,然后焙烧而成。
补充资料：陶瓷型铸造
用陶瓷浆料制成铸型生产铸件的铸造方法。陶瓷浆料由硅酸乙酯水解液和质地较纯、热稳定性较高的细耐火砂如电熔石英、锆英石、刚玉等混合而成。为使陶瓷浆料在短时间内结胶，常加入氢氧化钙或氧化镁作为催化剂。由于使用的耐火材料成分及其外观都与陶瓷相似，故称为陶瓷型。陶瓷型铸造是在普通砂型铸造基础上发展起来的一种新工艺。陶瓷型有两种类型：①陶瓷型全由陶瓷浆料浇灌而成。其制作过程是先将模样固定于型板上，外套砂箱，再将调好的陶瓷浆料倒入砂箱，待结胶硬化后起模,经高温焙烧即成为铸型。②采用衬套,在衬套和模样之间的空隙浇灌陶瓷浆料制造铸型。衬套可用砂型，也可用金属型。用衬套浇灌陶瓷壳层可以节省大量陶瓷浆料，在生产中应用较多。陶瓷型铸件表面粗糙度可达Ra10～1.25微米,尺寸精度高达3～5级,能达到少无切削加工的目的。陶瓷型铸造生产周期短，金属利用率高。最大铸件可达十几吨，主要用于铸造大型厚壁精密铸件和铸造单件小批量的冲模、锻模、塑料模、金属模、压铸模、玻璃模等各种模具。陶瓷型铸造模具的使用寿命可与用机械加工方法制成的模具相媲美，而制造成本则比用机械加工方法制成的模具低。