1) gel pre-carbonization
凝胶预碳化
1.
6Bi4Ti4O15) nanocrystalline powder with small particle size and good dispersion was prepared via the gel pre-carbonization sol-gel method.
用凝胶预碳化处理工艺的溶胶-凝胶法制备了晶粒粒径小且分散性能较好的钙锶铋钛(Ca0。
2) Carbonized RF aerogels(CRF aerogels)
碳化气凝胶
1.
Carbonized RF aerogels(CRF aerogels) have large specific area, good conductivityand excellent electro-chemical stability.
其政化产物碳化气凝胶（CRF气凝胶）具有大的比表面积、好的导电性和电化学稳定性，成为制备超级电化学双层电容器也（SEDLCs）的理想电极材料。
3) organic gel carbonization
有机凝胶碳化
1.
Several mesoporous control technologies of carbon materials have been summarized:catalytic activation,polymer blend carbonization,organic gel carbonization and template carbonization.
综合评述了国内外炭材料中孔控制方面的发展情况,总结提出了炭材料的几种中孔控制技术;催化活化法、共混聚合物碳化法、有机凝胶碳化法和模板碳化法。
4) carbon aerogel
碳气凝胶
1.
The microstructure of carbon aerogel was investigated by using electron scanning microscope(SEM),pore size distribution and electrical conductivity measurement.
探索新型纳米多孔材料碳气凝胶的微结构控制,研究常压条件下纤维增强型碳气凝胶的制备,以及催化剂浓度、质量分数、纤维表面特性、溶胶注入纤维前的老化时间等制备参数对其微结构的影响。
2.
This paper examins carbon aerogel by SEM, BET and cyclic voltammetry.
在常压条件下通过溶胶-凝胶法和碳化、活化工艺制备碳气凝胶材料。
3.
The micro structure of the porous carbon aerogels is measured by SEM and BET.
经高温碳化处理 ,将RF有机气凝胶转化为碳气凝胶 ,改变RC比和聚合单体的质量百分数 ,可控制气凝胶的粒径及孔径、密度及比表面积。
5) carbon aerogels
碳气凝胶
1.
For the first time,hydroquinone-formaldehyde aerogels have been prepared by sol-gel method and CO_2 supercritical drying,and after high temperature carbonization the carbonized carbon aerogels are obtained.
首次用溶胶-凝胶法和CO2超临界干燥技术制备了对苯二酚-甲醛有机气凝胶,并经高温碳化处理得到其碳气凝胶,测得气凝胶的比表面积由碳化前的375。
2.
In this paper, carbon aerogels are obtained through ordinary pressure drying; their structural properties are investigated.
碳气凝胶是一种新型多孔碳材料,具有比表面积大、电导率高的特点。
3.
SEM, BET and pore size distribution techniques were used to characterize the morphology and pore structure of the carbon aerogels.
研究了碳气凝胶在常压条件下的制备过程和干燥方法。
6) carbon-silica gel
碳硅凝胶
1.
Meso-tetrakis(4-aminophenyl)porphyrin[T(4-TAP)P] used as a suitable chelating reagent was loaded on the mixture of active carbon-silica gel.
首次以meso-四(4-氨基苯基)卟啉为衍生化试剂,使其负载于碳硅凝胶填充材料上,在优化的实验条件下,于pH9。
补充资料：碳化铍
分子式：Be2C
CAS号：
性质：固体物质。随游离碳含量和分散度不同而有黄、红、棕、灰等不同颜色，反萤石结构，晶格常数a=4.342×10-10m。熔点2200℃。沸点2528℃。在空气中稳定性比石墨高。在氩气中约于2400℃时开始熔化，在真空中于1400℃开始分解。室温下与水及水蒸气反应产生甲烷。1000℃以上与氮反应生成二氮化三铍。可缓慢溶于稀酸中。在1700℃惰性气氛下碳与铍作用或在1500℃～1900℃氩气氛下碳还原氧化铍生成。为制取铍化合物的原料。用作耐火材料。
CAS号：
性质：固体物质。随游离碳含量和分散度不同而有黄、红、棕、灰等不同颜色，反萤石结构，晶格常数a=4.342×10-10m。熔点2200℃。沸点2528℃。在空气中稳定性比石墨高。在氩气中约于2400℃时开始熔化，在真空中于1400℃开始分解。室温下与水及水蒸气反应产生甲烷。1000℃以上与氮反应生成二氮化三铍。可缓慢溶于稀酸中。在1700℃惰性气氛下碳与铍作用或在1500℃～1900℃氩气氛下碳还原氧化铍生成。为制取铍化合物的原料。用作耐火材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条