1) bisphenol A epoxy resin
双酚A型环氧树脂
1.
The effects of curing temperature and the content of on the curing speed of PSN-1 polysilazane/bisphenol A epoxy resin curing system were discussed.
研究了聚硅氮烷(PSN-1)/双酚A型环氧树脂固化体系的固化温度、PSN-1用量对固化速度的影响;并利用热重分析(TGA)研究了PSN-1用量对固化树脂高温残余质量分数的影响,对固化机理进行了初步探讨。
2) bisphenol A type epoxy resin
双酚A型环氧树脂
1.
The test conditions of determination of bisphenol A type epoxy resin by HPLC were established.
确定了高效液相色谱法分析双酚A型环氧树脂组成成分实验条件。
2.
Polyisocyanurate rigid foamed plastic modified by bisphenol A type epoxy resin has been prepared by isocyanate(MDI),polyether polyols(403,4110),bisphenol A type epoxy resin,foaming agent,foam homogeneoas reagent and other raw materials.
采用异氰酸酯(MDI)、聚醚多元醇(403、4110)、双酚A型环氧树脂、发泡剂、均泡剂等原料,制备了双酚A改性聚异氰脲酸酯硬质泡沫塑料。
5) liquid bisphenol-A diglycidyl ether
液态双酚-A型环氧树脂
1.
A new synthesis process of liquid bisphenol-A diglycidyl ether is designed,and the effect of various factors on the reaction course of E-51 epoxide resins is determined.
本文设计了一套新的液态双酚-A型环氧树脂的合成工艺,并探讨了合成E-51型环氧树脂的较佳反应条件,可以使生产每吨该树脂的ECH消耗量比现有国内工业水平减少60kg。
6) bisphenol A epoxy resin paint
双酚A型环氧树脂涂料
补充资料：双酚A型环氧树脂
双酚A型环氧树脂是由双酚A和环氧氯丙烷在氢氧化钠作用下缩聚而得。根据原料配比、反应条件及采用的方法取同，可制得不同聚合度的低分子量粘稠液体和高分子量、高软化点的固体。平均分子量300-7000。淡黄色或琥珀色透明粘稠液体或块状脆性固体。环氧树脂本身是热塑性线型聚合物．，受热时液体树脂粘度降低，固体树脂软化或熔溶。溶于丙酮、甲乙酮、环己团、醋酸乙酯苯、甲苯、二甲苯、无水乙醇．乙二醇等有机溶剂。环氧树脂分子中含有环氧基、羟基、醚键等极性基团．因而对金属、玻璃、陶瓷木材、织物、混凝土、玻璃钢等多种材料都有很强的粘接力。环氧树脂只有与固化剂作用，经固化后才能显示出优良的性能，粘接强度高，收缩率小，尺寸稳定，电绝缘性好，耐油、耐溶剂、耐碱、耐酸、耐水等。使用温度为-60～100 ℃，固化产物无毒、无味．对人体无害。环氧树脂的缺点是脆性较大．剥离强度很低．耐热性差．高温下容易降解。
用于配制环氧胶粘剂和密封剂。还用作酚醛树脂的改性剂、PVC塑溶胶的稳定剂、聚硫密封胶的增粘剂、氯磺化聚乙烯胶粘剂的硫化剂。