1) transformation induced plasticity
相变诱发塑性
1.
The elongation of the steel can be enhanced considerably due to strain induced martensite transformation and transformation induced plasticity (TRIP) when it is deformed at a temperature between M s and M d.
该钢在 Ms～ Md 温度之间形变 ,应变诱导相变 ,相变诱发塑性 (TRIP) ,其力学性能指标特别是伸长率大幅度提高。
2.
The steels show high strength as well as comprehensive plasticity because of strain induced phase transformation and transformation induced plasticity (TRIP) happened in the retained austenite in the steels.
在不含Ｃｒ，Ｎｉ的ＳｉＭｎ结构钢中，因残余奥氏体的应变诱导相变和相变诱发塑性，可得到良好的强度与塑性配合的综合性能·通过对二种成分ＳｉＭｎＴＲＩＰ钢力学性能的比较及其组织分析，探讨了ＴＲＩＰ效应提高结构钢力学性能的机理·结果表明，含有一定Ｍｎ合金元素的ＴＲＩＰ结构钢，当Ｓｉ含量小于２０％时，含Ｓｉ量愈高，其力学性能愈好
3.
When the steel changed in form between M s and M d,its tensibility enhanced considerably due to strain induced martensite transformations and transformation induced plasticity (TRIP) of retained austenite.
该钢在ＭｓＭｄ温度之间形变时，因残留奥氏体的应变诱导马氏体相变和相变诱发塑性ＴＲＩＰ，延伸率大幅度提高。
2) transformation-induced plasticity
相变诱发塑性
1.
Strain-induced transformation and transformation-induced plasticity behavior of retained austenite was discussed through observing the microstructures and examining the mechanical properties of both steels.
通过显微组织观察,力学性能分析,探讨了两种钢的应变诱导相变和相变诱发塑性行为。
2.
The behaviour of TRIP (transformation-induced plasticity) effect was discussed through observing microstructure, analyzing fracture morphology and comparing it with the mechanical properties of high-Si TRIP steels.
无硅TRIP钢采用临界区加热等温淬火热处理,获得铁素体,贝氏体及大量稳定残余奥氏体的三相组织·通过对其显微组织观察,断口形貌分析,与高硅TRIP钢力学性能的相互比较,探讨了无硅TRIP钢相变诱发塑性的行为·结果表明:无硅TRIP钢在拉伸变形过程中,应变诱导相变,相变诱发塑性;其拉伸断口形貌呈韧性断口特征;经790℃加热在400℃等温5min时,抗拉强度达到754MPa,延伸率达到36%,综合性能(强塑积)达到27144MPa%的最高值
3.
The behaviour of transformation-induced plasticity were discussed through observing the microstructure, and analyzing the mechanical properties of TRIP steel replacing Si by Al.
通过对其显微组织观察、力学性能分析,探讨了以A1代Si的TRIP钢的相变诱发塑性的行为。
3) TRIP
[英][trɪp] [美][trɪp]
相变诱发塑性
1.
68Mn (mass%) TRIP steel have been investigated at room temperature.
6×10-6s-1时,高碳硅锰TRIP钢伸长率由14%～15%提高到22%左右;屈服强度由1015MPa提高到1198MPa;抗拉强度由1448MPa提高到1546MPa;拉伸试样中残留奥氏体量减少,这表明在低应变速率下应变诱导相变、相变诱发塑性能充分进行。
4) TRIP steel
相变诱发塑性钢
1.
The FLD and mechanical properties under high speed impact for low carbon TRIP steel were studied.
对抗拉强度600 MPa级的低碳相变诱发塑性钢(TRIP钢)进行了拉伸、成形、高速冲击拉伸和激光焊接试验。
5) transformation induced plasticity (TRIP)
相变诱发塑性(TRIP)
6) transformation induced plasticity (TRIP)steel
相变诱发塑性TRIP钢
补充资料：λ相变
分子式：
CAS号：
性质：低温时，液态氦(4He)有两个不同的液相，He-I和He-II。He-I是一个正常液体，而He-II是一个超流体，因为它流动时没有黏度。He-I和He-II之间的相转变是连续性相变，也称λ相变。
CAS号：
性质：低温时，液态氦(4He)有两个不同的液相，He-I和He-II。He-I是一个正常液体，而He-II是一个超流体，因为它流动时没有黏度。He-I和He-II之间的相转变是连续性相变，也称λ相变。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条