1) polytrimethylene terephthalate fiber
聚对苯二甲酸丙二酯纤维
2) polytrimethylene terephthalate fiber
聚对苯二甲酸丙二醇酯纤维
3) polyester fiber
聚对苯二甲酸乙酯纤维
4) poly-1,4-cyclohexane dimethylene terephthalate fiber
聚对苯二甲酸-1,4-环己二甲酯纤维
5) poly(trimethylene terephthlate)
聚对苯二甲酸丙二酯
1.
Decabromodiphenyl ethane(DBDPE),decabromodiphenyl oxide(DBDPO),and tris(tribro- mophenoxy)triazine(TBPC)were separately mixed with Sb_2O_3 and introduced into poly(trimethylene terephthlate)(PTT)through extrusion as flame retardants.
采用十溴二苯乙烷、十溴二苯醚和三(三溴苯氧基)三嗪分别与三氧化二锑复配,经双螺杆挤出机熔融共混制备阻燃聚对苯二甲酸丙二酯(PTT)复合材料,研究了阻燃剂的种类和用量对 PTT 结构性能的影响。
6) polytrimethylene terephthalate
聚对苯二甲酸丙二醇酯
1.
Investigation on the depolymerization of polytrimethylene terephthalate in methanol;
聚对苯二甲酸丙二醇酯的甲醇解聚研究
2.
The alloy of polycarbonate (PC)/polytrimethylene terephthalate (PTT) was modified with four different impact modifiers and compared with the imported PC/polybutylene terephthalate and PC/polyethylene terephthalate samples.
针对聚碳酸酯(PC)/聚对苯二甲酸丙二醇酯(PTT)共混合金相容性差的缺点,采用了4种不同的抗冲改性剂对其进行增韧改性,并与PC/聚对苯二甲酸丁二醇酯、PC/聚对苯二甲酸乙二醇酯进行性能比较。
3.
The melting behavior of polyethylene-2,6-naphthalate/polytrimethylene terephthalate(PEN/PTF)blends at different ratios was studied with a differential scanning calorimeter.
利用差示扫描量热仪对不同配比的聚萘二甲酸乙二醇酯/聚对苯二甲酸丙二醇酯(PEN/PTT)共混体系的熔融行为进行了分析,发现在共混体系中两组分形成各自的晶体,PEN和PTT的熔点均随另一组分含量的增加而下降。
补充资料：聚对苯二甲酸丙二酯纤维
分子式：
CAS号：
性质：聚酯纤维的一种。指由对苯二甲酸二甲酯与1,3-丙二醇缩聚生成的聚对苯二甲酸丙二酯为原料制得的纤维。该纤维的性能介于聚对苯二甲酸乙二酯纤维(PET纤维)和聚酰胺纤维(PA66和PA6纤维)之间，兼具二者的优点；熔点228℃。玻璃化温度55℃。能在95℃左右用分散染料进行无载体染色；纤维强度比聚对苯二甲酸乙二酯纤维稍低(约3.4cN/dtex)，伸长率20％～25％，初始模量明显低于PET纤维(约25cN/dtex)，受拉后的弹性恢复极好；主要被用于制作地毯，也有用于制作与棉、毛的混纺织物。
CAS号：
性质：聚酯纤维的一种。指由对苯二甲酸二甲酯与1,3-丙二醇缩聚生成的聚对苯二甲酸丙二酯为原料制得的纤维。该纤维的性能介于聚对苯二甲酸乙二酯纤维(PET纤维)和聚酰胺纤维(PA66和PA6纤维)之间，兼具二者的优点；熔点228℃。玻璃化温度55℃。能在95℃左右用分散染料进行无载体染色；纤维强度比聚对苯二甲酸乙二酯纤维稍低(约3.4cN/dtex)，伸长率20％～25％，初始模量明显低于PET纤维(约25cN/dtex)，受拉后的弹性恢复极好；主要被用于制作地毯，也有用于制作与棉、毛的混纺织物。