1) poly-1,3-trimethylene terephthalate
聚对苯二甲酸-1,3-丙二酯
2) poly(1,3-trimethylene terephthalate)
聚对苯二甲酸-1,3-丙二醇酯
1.
An antistatic poly(1,3-trimethylene terephthalate)(PTT) was synthesized from purified terephthalic acid(PTA), 1,3-propanediol(PDO) and antistatic agent via direct esterification.
采用精对苯二甲酸(PTA)、1,3-丙二醇(PDO)及抗静电剂直接酯化法合成具有抗静电性能的聚对苯二甲酸-1,3-丙二醇酯(PTT)。
3) poly(trimethylene terephthlate)
聚对苯二甲酸丙二酯
1.
Decabromodiphenyl ethane(DBDPE),decabromodiphenyl oxide(DBDPO),and tris(tribro- mophenoxy)triazine(TBPC)were separately mixed with Sb_2O_3 and introduced into poly(trimethylene terephthlate)(PTT)through extrusion as flame retardants.
采用十溴二苯乙烷、十溴二苯醚和三(三溴苯氧基)三嗪分别与三氧化二锑复配,经双螺杆挤出机熔融共混制备阻燃聚对苯二甲酸丙二酯(PTT)复合材料,研究了阻燃剂的种类和用量对 PTT 结构性能的影响。
4) polytrimethylene terephthalate
聚对苯二甲酸丙二醇酯
1.
Investigation on the depolymerization of polytrimethylene terephthalate in methanol;
聚对苯二甲酸丙二醇酯的甲醇解聚研究
2.
The alloy of polycarbonate (PC)/polytrimethylene terephthalate (PTT) was modified with four different impact modifiers and compared with the imported PC/polybutylene terephthalate and PC/polyethylene terephthalate samples.
针对聚碳酸酯(PC)/聚对苯二甲酸丙二醇酯(PTT)共混合金相容性差的缺点,采用了4种不同的抗冲改性剂对其进行增韧改性,并与PC/聚对苯二甲酸丁二醇酯、PC/聚对苯二甲酸乙二醇酯进行性能比较。
3.
The melting behavior of polyethylene-2,6-naphthalate/polytrimethylene terephthalate(PEN/PTF)blends at different ratios was studied with a differential scanning calorimeter.
利用差示扫描量热仪对不同配比的聚萘二甲酸乙二醇酯/聚对苯二甲酸丙二醇酯(PEN/PTT)共混体系的熔融行为进行了分析,发现在共混体系中两组分形成各自的晶体,PEN和PTT的熔点均随另一组分含量的增加而下降。
5) poly(trimethylene terephthalate)
聚对苯二甲酸丙二醇酯
1.
Spinning Process of Poly(trimethylene terephthalate) Filament;
聚对苯二甲酸丙二醇酯长丝生产工艺
2.
The crystallization behavior of poly(trimethylene terephthalate) (PTT) containing various nucleation agents was studied by means of Differential Scanning Calorimetry (DSC), Depolarized Light Intensity(DLI) technique and Polarized Light Microscopy (PLM).
采用差示扫描量热(DSC)、解偏振光强度(DLI)和偏光显微镜(POM)等方法研究了含不同成核剂聚对苯二甲酸丙二醇酯(PTT)的结晶行为。
3.
Poly(trimethylene terephthalate)(PTT), a new material, is a promising polymer with potential applications.
新型聚酯材料聚对苯二甲酸丙二醇酯 (PTT)是一种极有应用潜力的聚合物 ,但在非纤维领域的研究与应用才刚开始。
6) poly(trimethylene terephthalate)
聚对苯二甲酸丙二酯
1.
A kind of flame retardant and glass fiber reinforced poly(trimethylene terephthalate)(PTT) engineering plastic was prepared .
研制了一种30%玻纤增强阻燃聚对苯二甲酸丙二酯(PTT)工程塑料,重点考察了增韧剂、结晶成核剂、其它聚酯及溴锑复合阻燃剂对PTT性能的影响。
2.
Thermal spectra of poly(trimethylene terephthalate)(PTT) were collected over a temperature range of 40 ℃~250 ℃ by FT-IR micro-spectroscopy.
采用显微傅立叶转换红外光谱技术研究了聚对苯二甲酸丙二酯(PTT)的熔融相转变过程。
3.
The processes for solid state polymerization and glass fiber reinforcement of poly(trimethylene terephthalate)(PTT) were researched.
初步研究了聚对苯二甲酸丙二酯 (PTT)固相聚合及其玻璃纤维 (GF)增强工艺 ,探讨了PTT的热稳定性及GF含量和树脂特性粘度对GF增强PTT性能的影响 ,并对PTT与聚对苯二甲酸丁二酯 (PBT)增强前后的性能进行了比较。
补充资料：聚对苯二甲酸丁二酯/聚碳酸酯共混物
分子式：
CAS号：
性质： PC与PBT都是聚酯类聚合物，机械共混时必须把原料充分干燥且避免温度过高以及在受热状态下停留时间过长，否则将因发生酯交换反应导致共混物性能劣化。另外的对策是加入各种稳定剂以阻止酯交换反应的发生。当PC含量很少时体系是部分相容的，PC占30％～40％时则完全相容，若PC含量比较多而又少于30％时，PBT/PC共混体系成为PBT；PC、PBT/PC相容物的共混体系。PBT中加入PC对冲击强度的提高尚不很突出，若同时加人橡胶类物质，则增韧效果更好。PC的加入使得PBT结晶度下降，对PBT因结晶引起制品易翘曲变形的特点得以改善，这种效果对于玻璃纤维增强PBT尤其重要。
CAS号：
性质： PC与PBT都是聚酯类聚合物，机械共混时必须把原料充分干燥且避免温度过高以及在受热状态下停留时间过长，否则将因发生酯交换反应导致共混物性能劣化。另外的对策是加入各种稳定剂以阻止酯交换反应的发生。当PC含量很少时体系是部分相容的，PC占30％～40％时则完全相容，若PC含量比较多而又少于30％时，PBT/PC共混体系成为PBT；PC、PBT/PC相容物的共混体系。PBT中加入PC对冲击强度的提高尚不很突出，若同时加人橡胶类物质，则增韧效果更好。PC的加入使得PBT结晶度下降，对PBT因结晶引起制品易翘曲变形的特点得以改善，这种效果对于玻璃纤维增强PBT尤其重要。