1) covering power
深镀能力
1.
The process has greater covering power than cyanide copper plating process by comparison.
通过比较该工艺与氰化镀铜工艺的深镀能力,可知前者深镀能力明显优于后者。
2.
Throwing power,covering power,bright deposit current density range and cathodic current efficience of the bath were measured.
以碘酸钾、三氯乙酸、甘氨酸和甲酸为添加剂,加入到标准镀铬液中,测定了镀液的分散能力、光亮电流密度范围、深镀能力、阴极电流效率。
2) throwing power
深镀能力
1.
The results show that throwing power can be effectively improved in copper plating for the small holes of high aspect ratio PCB by taking bottom erupting way and clamp vibrating measures.
高厚径比PCB的电镀加工中,深镀能力越来越成为一个重要的评价指标。
2.
The throwing power of the bath is 100%.
试验结果表明,电流效率在90%左右,并随电流密度、温度和pH的提高而增大;镀液深镀能力达100%。
3) throwing power
均镀能力
1.
64 times as that of the conventional technology, and the throwing power is increased 7.
６３８倍，均镀能力提高７。
2.
And raising the concentration of cuprous cya- nide as the main salt is helpful to increasing the current efficiency and throwing power and reducing the electroplating cost as well.
5g/L可以将碳酸钠浓度控制在工艺范围内;降低镀槽电压和增加阳极面积有利于降低碳酸钠的浓度;较高的主盐浓度可以提高镀液的电流效率和均镀能力,有利于降低电镀成本。
4) drilling ability
钻深能力
1.
Discussion on the improvement of rig drilling ability with middle or deep depth;
中深井石油钻机钻深能力探讨
6) depth capability
潜深能力
补充资料：深镀能力
分子式：
CAS号：
性质：又称深镀能力。在给定条件下，电镀液在整个阴极表面最初沉积金属的能力。是电镀液的重要性能之一，可通过多种方法进行测量。如直角阴极法：可选用厚度为0.2mm，100mm×50mm的软钢板或铜板作阴极，阴极背面绝缘，测定时将其弯成直角形，正对阳极浸入镀液进行电镀。经一定时间后，以直角阴极表面镀上金属的面积百分数评定镀液覆盖能力的优劣。此法适于测定覆盖能力差的镀液。对覆盖能力较好的镀液可采用内孔法：用一定内径(如ф10mm×100mm)的低碳钢管或铜管作为试样，管的内径正对阳极，直接放在生产镀槽中电镀，经一定时间后纵向锯开管子，根据管内表面镀上镀层的深度和面积评定镀液覆盖能力的优劣。
CAS号：
性质：又称深镀能力。在给定条件下，电镀液在整个阴极表面最初沉积金属的能力。是电镀液的重要性能之一，可通过多种方法进行测量。如直角阴极法：可选用厚度为0.2mm，100mm×50mm的软钢板或铜板作阴极，阴极背面绝缘，测定时将其弯成直角形，正对阳极浸入镀液进行电镀。经一定时间后，以直角阴极表面镀上金属的面积百分数评定镀液覆盖能力的优劣。此法适于测定覆盖能力差的镀液。对覆盖能力较好的镀液可采用内孔法：用一定内径(如ф10mm×100mm)的低碳钢管或铜管作为试样，管的内径正对阳极，直接放在生产镀槽中电镀，经一定时间后纵向锯开管子，根据管内表面镀上镀层的深度和面积评定镀液覆盖能力的优劣。