1) hot compression deformation
高温压缩变形
1.
WTThe flow stresses of Cu15Ni8Sn(Zr) alloy treated by two different kinds of heat treatment process during hot compression deformation were measured and analyzed respectively.
33s-1的试验条件下,测定了两种热处理状态的Cu 15Ni 8Sn(Zr)合金的高温压缩变形流动应力,并进行了分析。
2) warm compression deformation
温压缩变形
1.
Spheroidization behavior of cementite during warm compression deformation;
温压缩变形过程中渗碳体的球化行为
3) thermo compression set
高温压缩永久变形
1.
In this paper,the influence of the ratio of the CR/PUR blends on the curing characteristic,mechanical property,hot ageing resistance and thermo compression set of the blends were studied.
研究了共混比对氯丁橡胶/聚氨酯橡胶(CR/PUR)的硫化特性,硫化胶力学性能、耐热老化性能以及高温压缩永久变形的影响。
4) compression set test at high temperature
高温压缩永久变形试验
5) hot compression deformation behaviors
高温压缩变形行为
1.
The hot compression deformation behaviors of composites with different SnO_2 coating contents were also investigated, and the textures of the compressed composites were performed.
利用X射线衍射、扫描电镜、能谱以及透射电镜等方法对晶须表面涂层和复合材料的界面结构进行了研究;分析了SnO_2涂层含量对复合材料挤压铸造性能、常温拉伸性能以及热膨胀性能的影响规律;探讨了SnO_2涂层含量对复合材料高温压缩变形行为的影响机制,并对压缩变形后复合材料的织构进行了测定。
6) high temperature compression
高温压缩
1.
Microstructure evolution of AZ91D magnesium alloy during high temperature compression;
AZ91D镁合金高温压缩过程中的微观组织演变
2.
In order to improve the mechanical properties,firstly the elastic plastic deformation behavior of TiB 2 40Cu 8Ni cermet in high temperature compression was studied.
为进一步提高复合材料的力学性能 ,首先研究了TiB2 4 0Cu金属 -陶瓷高温压缩弹塑性变形行为 ,证明了高陶瓷体积分数下金属陶瓷在高温环境中具有一定的塑性行为 ;然后分别在 12 0 0℃、12 5 0℃、130 0℃温度下对复合材料进行二次热压 ,详细研究了TiB2 4 0Cu 8Ni复合材料液 -固两相区间的变形行为、组织特征及力学性能的变化。
补充资料：变形高温合金
变形高温合金
wrought superalloy
b lonx一ng gaowen heJ一n变形高温合金(wrought superalloy)能够通过热加工变形成型的高温合金材料。一般分为铁基变形高温合金、镍基变形高温合金和钻基变形高温合金3类。 铁基变形高温合金广泛用作燃烧室、涡轮盘、机匣和轴等零件，多数是从Fe一Cr一Ni系添加合金化元素发展起来的。中国发展此类合金的牌号较多，板材合金有GHi一40、GHlo15、GHioi6、GHZo18等;棒材合金有GHZ13o和GH23oZ;盘材合金有GHZ135、GH761等。一般适用于工作温度较低的发动机。 镍基变形高温合金发展较快，应用最广泛，一般以Ni一cr固溶体为基体添加多种合金元素发展起来的。此类合金，牌号甚多。中国自己研制成功的有GH151棒材合金;GHz7、GH3128、GH一70板材合金;GH4133盘材合金等。 钻基变形高温合金在中国发展较少，一般不研制新合金，这是因为钻资源缺乏。这类合金的焊接性能及抗热疲劳、抗氧化、抗冲刷和耐蚀等性能都较好，主要用于导向叶片。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。