1) thermal shock resistance
抗热震性
1.
Thermal shock resistance of nano BN-SiC composites;
纳米BN复合SiC材料的抗热震性研究
2.
Effect of ZrO_2-SiC composite powder addition on thermal shock resistance of Al_2O_3-C refractories;
添加ZrO_2-SiC复合粉体对Al_2O_3-C质耐火材料抗热震性能的影响
3.
Research on preparation technology and thermal shock resistance of Al_2O_3/cordierite ceramics;
Al_2O_3/堇青石陶瓷的制备和抗热震性能研究
2) Resistance to thermal shock
抗热震性
1.
The study shows that the resistances to thermal shock and to slag corrosion of the β-Sialon/SiC are better than β-Sialon/corundum, the fracture times of the resistance to thermal shock are up to 40.
结果表明:β-Sialon/SiC的抗热震性、抗渣侵蚀性优于β-Sialon/刚玉,在1100℃时,抗热震断裂次数达到40次以上。
2.
the characters of sic and the appliance are introduced,the influence on the resistance to thermal shock of kiln furniture is studied through experiments.
本文介绍了碳化硅的特点及其在窑具中的应用 ,通过试验探讨了其对窑具抗热震性的影
3) thermal shock
抗热震性
1.
The result shows that the coating,having high emissivity,bonds well with substrate and have better property of thermal shock resistance than Al2O3-SiC ceramic coating.
结果表明,该涂层有很高的发射率,与基材结合良好,抗热震性能明显优于Al2O3-SiC陶瓷涂层。
2.
The influences of RE2(CO3)3 content on the sintering temperatures,thermal shock,the bulk density on the solution and the phase comp.
以碳化硅、高岭土、氧化铝粉为原料,以质量分数为3%的混合碳酸稀土为助熔剂,烧制具有气孔率高、容重小、强度高、抗热震性高的莫来石-碳化硅质泡沫陶瓷过滤器。
4) high resist heat quake character
高抗热震性
1.
The beehive bodies hare high resist heat quake character and high regenerative heat character.
以红柱石为主要原料,不需加任何添加剂,采用独特的模挤压工艺成型,可制作出任意孔径和壁厚的蜂窝体,并具备了高抗热震性和高蓄热量性能。
5) thermal shock resistance
抗热震性能
1.
Microstructure and thermal shock resistance of YPSZ gradient coating fabricated by plasma spraying
等离子喷涂YPSZ陶瓷梯度涂层的组织与抗热震性能
2.
The thermal shock resistance of plasma-sprayed ZrO2 thermal barrier coatings under the conditions of water quenching and flame jet was studied.
为了进一步了解等离子喷涂ZrO2涂层的制备及失效控制措施,提高涂层的使用寿命,研究了涂层在水淬和火焰喷烧两种条件下的抗热震性能。
3.
The thermal stress fracture resistance factor R is used to characterize the thermal shock resistance of the ceramic material.
抗热震性能是结构陶瓷材料的重要性能之一。
6) thermal-shock resistance
抗热震性能
1.
Its thermal-shock resistance was studied.
分别采用超音速火焰喷涂技术(HVOF)与大气等离子喷涂技术(APS)喷涂NiCrAlY粘结底层和纳米氧化锆工作面层获得了典型的双层结构热障涂层,并采用设计试验对其抗热震性能进行了研究。
2.
Density,porosity,hardness and thermal-shock resistance was measured.
通过对样片密度、气孔率和硬度的测定,以及对试验材料显微结构的观察,分析了烧结助剂、粉体制备工艺和烧结工艺对氧化镁陶瓷抗热震性能的影响。
3.
The thermal-shock resistance of Al2O3,Al2O3/TiC and cobalt-coated Al2O3/TiC composites were studied by residual-strength method.
采用急冷-强度法表征了单相Al2O3、Al2O3/TiC及Co包覆Al2O3/TiC三种材料的抗热震性能。
补充资料：抗热震性
抗热震性
thermal shock resistance
kangrezhenxing抗热展性(thermal shoek resistanee)材料在温度急剧变化条件下抵抗损伤的能力。曾称热稳定性，热展稳定性，抗热冲击性，抗温度急变性，耐急冷急热性等。 衬火材并在低温和中温下是脆性材料，缺乏延性，在热工设备使用中，常常受到急剧的温度变化，导致损伤。抗热震性是耐火材料重要的使用性能之一。 抗热震性机理材料的抗热震性，是其力学性能与热学性能在温度变化条件下的综合表现。 材料遭受的急剧温度变化，称为热震。材料在热震中产生的新裂纹，以及新裂纹与原有裂纹扩展造成的开裂、剥落、断裂等状况，称为热震损伤。热震损伤是热应力作用的结果。材料在温度变化时，变形受到抑制所产生的应力为热应力。线脚胀来数不同的多相物体在温度变化时，均匀热膨胀的物体受到温度梯度作用时，以及相变时，都会产生热应力。热应力与材料的弹性模贡及弹性应变成正比，而弹性应变等于线膨胀系数和温度变化的乘积。在无限平板中 Ea(T，一T:) 口“二二二— 上一产式中如为热应力，Pa;E为弹性模量，Pa;a为线膨胀系数，K一，;T，为最终温度，℃;T;为初始温度，℃;产为泊松比。 理论上，对陶瓷与耐火材料处于脆性阶段的抗热震性已提出两种互补的分析。一种是热弹性理论，认为材料受到的热应力超过材料的极限强度时，导致瞬时断裂，即所谓的“热震断裂”。金格里(W.D.Kingery)根据不同的热震条件，导出“抗热展断裂参数”R，侧和R”表达式: R一些鉴丝(适用于剧烈受热或冷却条件) Ea、~产’JJ旧切卜、，~八、弓~‘，一r~”’ 。，af(1一产)孟、。 R子=己二二言=;=~从 Ea’~‘ (适用于缓和受热或冷却条件) 。，价(1一产)又。 R"~习二.气===女‘~aR EaC，P (适用于恒速受热或冷却条件)式中价为断裂强度;人为热导率;C，为质量定压热容;，为密度;。一燕，为热扩散率。对氧化物陶瓷等特殊·-一一’‘户P-一-衬火材抖，为避免热展断裂的发生，要求具有较高的强度、热导率或热扩散率，以及低的线膨胀系数和弹性模量。另一种是能量理论，认为材料中不可避免地存在着或大或小数量不等的微裂纹，材料的热震损伤是裂纹扩展的结果。哈塞曼(D.P.H.Hasselman)用断裂力学中的能量平衡原理分析热应力引起的裂纹扩展，导出“抗热展损伤参数”R牌和Rllll表达式: 。