1) thermal shock resistance
热震抗力
1.
The existence of the net in Al2O3/Nb interface was able to increase the thermal shock resistance of the joint considerably.
首次研究了在Ａｌ２Ｏ３／Ｎｂ的钎焊界面之间加入一层金属Ｍｏ网，可大幅度提高接头的热震抗力，经用Ｎｉ５１Ｔｉ４９钎料焊接后，７００℃淬水后的剩余强度达到了不加网的焊后强度，强度提高了１８０％以上，用Ｃｕ５２Ｎｉ１８Ｔｉ３０钎料焊接并加Ｍｏ网后，７００℃淬水后的剩余强度也提高了１３０％以上。
2) thermal shock fatigue resistance
热震疲劳抗力
1.
The effects of TiC content on the thermal shock fatigue resistance were studied.
研究了Al2O3-TiC复合陶瓷的热震疲劳机制和TiC的添加量对其热震疲劳抗力的影响。
3) thermal shock resistance
抗热震性
1.
Thermal shock resistance of nano BN-SiC composites;
纳米BN复合SiC材料的抗热震性研究
2.
Effect of ZrO_2-SiC composite powder addition on thermal shock resistance of Al_2O_3-C refractories;
添加ZrO_2-SiC复合粉体对Al_2O_3-C质耐火材料抗热震性能的影响
3.
Research on preparation technology and thermal shock resistance of Al_2O_3/cordierite ceramics;
Al_2O_3/堇青石陶瓷的制备和抗热震性能研究
4) thermal shock resistance
抗热震
1.
Ablation and thermal shock resistance properties of C/SiC jet vane;
碳/碳化硅燃气舵的烧蚀及抗热震性
2.
The thermal shock resistance lifetime of coatings was tested by thermoshock cyclic method.
运用XRD、SEM、TEM、拉曼光谱和金相技术等分析手段对涂层的显微结构、物相组成进行了观察与分析;利用热冲击试验测试涂层的抗热震寿命。
3.
The effects of Al2O3 additive and its contents on thermal shock resistance of ZrO2 ceramics were investigated.
对氧化锆陶瓷材料的抗热震性能进行了研究,探讨了Al2O3添加剂的含量对氧化锆陶瓷材料的抗热震性能的影响。
5) Resistance to thermal shock
抗热震性
1.
The study shows that the resistances to thermal shock and to slag corrosion of the β-Sialon/SiC are better than β-Sialon/corundum, the fracture times of the resistance to thermal shock are up to 40.
结果表明:β-Sialon/SiC的抗热震性、抗渣侵蚀性优于β-Sialon/刚玉,在1100℃时,抗热震断裂次数达到40次以上。
2.
the characters of sic and the appliance are introduced,the influence on the resistance to thermal shock of kiln furniture is studied through experiments.
本文介绍了碳化硅的特点及其在窑具中的应用 ,通过试验探讨了其对窑具抗热震性的影
6) thermal shock
抗热震性
1.
The result shows that the coating,having high emissivity,bonds well with substrate and have better property of thermal shock resistance than Al2O3-SiC ceramic coating.
结果表明,该涂层有很高的发射率,与基材结合良好,抗热震性能明显优于Al2O3-SiC陶瓷涂层。
2.
The influences of RE2(CO3)3 content on the sintering temperatures,thermal shock,the bulk density on the solution and the phase comp.
以碳化硅、高岭土、氧化铝粉为原料,以质量分数为3%的混合碳酸稀土为助熔剂,烧制具有气孔率高、容重小、强度高、抗热震性高的莫来石-碳化硅质泡沫陶瓷过滤器。
补充资料：不可抗力
| 不可抗力 force majeure 当事人自身能力不能抗拒也无法预防的客观情况或事故。不可抗力可以是自然原因酿成的，也可以是人为的、社会因素引起的。前者如地震、水灾、旱灾等，后者如战争、政府禁令、罢工等。不可抗力所造成的是一种法律事实。当不可抗力事故发生后，可能会导致原有经济法律关系的变更、消灭，如必须变更或解除经济合同；也可能导致新的经济法律关系的产生，如财产投保人在遇到因不可抗力所受到的在保险范围内的财产损失时 ，与保险公司之间产生出赔偿关系。当不可抗力事故发生后，遭遇事故一方应采取一切措施，使损失减少到最低限度。在订立买卖合同时，一般都订有不可抗力条款，其内容包括：不可抗力内容；遭到不可抗力事故的一方 ，向另一方提出事故报告和证明文件的期限和方式；遭遇不可抗力事故一方的责任范围。如因不可抗力使合同无法履行，则应解除合同。如不可抗力只是暂时阻碍合同履行，则一般采取延期履行合同的方式。凡发生不可抗力事故，当事方已尽力采取补救措施但仍未能避免损失的情况下，可不负赔偿责任。 |