1) impact corrosion and abrasion
冲击腐蚀磨损
1.
The impact corrosion and abrasion behavior of three steels for liner were investigated under different impact energy in ironstone slurry.
对三种湿磨衬板钢的冲击腐蚀磨损性能与机制的研究结果表明:冲击功增大,其磨损失重呈不同程度的增大;在2 0J冲击功下,三种钢的磨损失重相差不大;2 7J与3 5J时低碳高合金钢的磨损失重明显较小。
2.
The impact corrosion and abrasion properties of the low carbon alloy steels with different chromium content under the simulated working condition of metallurgical industry were investigated by MLD-10 impact-corrosion-abrasion tester.
2J冲击功下,低碳合金钢的冲击腐蚀磨损机制为:短时间内为累积变形引起的材料的浅层剥落,长时间后转变为多次塑变造成的表面硬化层的去除;在2。
2) corrosive impact abrasion
冲击腐蚀磨损
1.
Comparison of corrosive impact abrasion behavior between low carbon high alloy steel and high manganese steel;
低碳高合金钢和高锰钢冲击腐蚀磨损特性研究
3) impact-corrosion-wear
冲击腐蚀磨损
1.
Investigation on impact-corrosion-wear property of two kind of steels;
两种钢冲击腐蚀磨损性能的试验研究
2.
A comparision of impact corrosion and wear praperties is made between high chromium cast iron and low corbon high alloy steel by the modified MLD-10 impact-corrosion-wear tester.
在改进后的MLD -10型冲击腐蚀磨损试验机上 ,对高铬铸铁和低碳高合金钢的耐冲击腐蚀磨损性能进行比较研究 ,通过不同条件下材料的失重、冲击磨损面的形貌、材料冲击端表层及亚表层的组织结构变化等来研究 2种材料的抗冲击腐蚀磨损性能 ,着重研究浆料性质、冲击功大小等对 2种材料抗冲击腐蚀磨损性能的影响。
4) corrosion and impact erosion-wear
腐蚀冲击磨损
5) corrosion and erosion-wear resisting
耐腐蚀冲击磨损
补充资料：腐蚀磨损
在摩擦过程中伴有腐蚀作用的一种磨损。金属件表面在液体、气体或润滑剂中发生化学或电化学反应，形成较易被磨损或剥离的腐蚀产物，在摩擦过程中腐蚀产物被剥离,暴露出的新的金属面又进入新的化学反应,如此交替出现腐蚀和磨损而使材料损失。腐蚀磨损的破坏作用大大超过单纯的腐蚀或磨损。一般金属洁净表面与空气接触后生成氧化膜，多数金属表面氧化膜的厚度为0.01微米。当磨损速度低于氧化膜厚度的增长速度时，氧化和磨损尚不相互促进，膜层可起保护作用。当磨损速度超过氧化速度，腐蚀磨损便变得剧烈。但氧化膜又不宜过厚，否则易于脆性断裂,形成硬的氧化物磨粒,使磨损加速。腐蚀磨损与环境、温度、滑动速度、载荷和润滑条件有关，相互关系极为复杂。如内燃机轴承在湿空气中容易生锈，在润滑剂中工作也常会出现腐蚀磨损。在特殊介质中工作的选矿机械和化工机械等的零件更常出现严重的腐蚀磨损。防止腐蚀磨损应从选材（如用不锈钢和耐蚀合金等）、表面保护处理、降低表面工作温度和选择适当的润滑剂等入手。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。