1) composite film
复合薄膜
1.
Expandable graphite-filled polymer (LDPE) composite film materials for flame retardancy;
EG填充无卤阻燃型LDPE复合薄膜阻燃性能研究
2.
Preparation and anticoagulation evaluation of emodin/poly(lactic acid) composite films;
大黄素/聚乳酸物复合薄膜的制备及抗凝血研究
3.
Structure and properties of MoS_2-Ti composite films deposited by unbalanced magnetron sputter ion plating;
非平衡磁控溅射离子镀MoS_2-Ti复合薄膜的结构及性能
2) Composite thin films
复合薄膜
1.
ITO/TiO2/CdS composite thin films were successfully prepared in aqueous system by electrodeposition of CdS nanoparticles on ITO/TiO2substrate.
实验表明,电镀液的组成、实验温度可影响薄膜中CdS纳米粒子的生长,从而使不同条件获得的复合薄膜电极的光电转换效率不同,实验温度为40℃、电镀液的组成为CCd2+=0。
2.
The uniform and transparent nanometer TiO2/SiO2 composite thin films were prepared successfully on clear glass in this paper.
用溶胶-凝胶法在清洁的玻璃表面成功制备了均匀透明的纳米TiO2/SiO2复合薄膜,并用扫描电镜,红外光谱仪,综合热分析仪和接触角测定仪对薄膜的结构和性质进行了研究。
3) composite films
复合薄膜
1.
TiO2-SiO2 composite films is prepared doping a cationic surfactant cetyltrimethlammonium bromide(CTAB) by solgel method.
利用红外光谱(IR)研究掺杂薄膜表面结构特征;紫外分光光度计UV-VIS-NIR研究不同实验条件下制备的复合薄膜吸收透过性的影响;利用反射式椭圆偏振光谱仪(ELLIP)测试薄膜的椭偏参数及Cauchy模型对椭偏参数进行计算机数据拟和,获得了掺杂的TiO2-SiO2复合薄膜光学常数在300-700nm波长范围的色散关系。
2.
Optical behavior of composite films was researched.
讨论了纳米TiO2在线型低密度聚乙烯(LLDPE)/低密度聚乙烯(LDPE)复合体系中的分散和体系流变行为,研究了复合薄膜的光学性能。
4) composite thin film
复合薄膜
1.
Preparation and characterization of PANI/CuTsPc composite thin films by layer-by-layer self-assembly
聚苯胺/磺化酞菁铜自组装复合薄膜的制备与表征
2.
Optical absorption characteristics of nanometer-sized metal particles dispersed composite thin films are investigated based on the Mie scattering theory.
根据M ie散射理论,研究了金属纳米颗粒镶嵌在载体介质中的复合薄膜的光吸收特性,计算得到Cu的介电常数与波长的关系。
3.
The results indicated that ZnO/TiO2 composite thin film with good crystal and absorption spectrum can be obtained after dipped in Zn(Ac)2 for 3 h with proper heat treatment,and.
用丝网印刷结合溶胶凝胶法制备了多孔TiO2薄膜,用溶液浸渍法制备了ZnO/TiO2复合薄膜;对薄膜的热处理制度、表面形貌、横断面结构、吸光度等进行了分析;组装电池,测试了电池的光电性能,结果表明:浸渍Zn(Ac)23 h,经过适当的热处理后,可以形成结晶良好,吸光度较好的ZnO/TiO2复合薄膜,电池的开路电压,短路电流以及光电转换效率均得到较大的提高。
5) laminated films
复合薄膜
1.
Application of Aqueous PU Adhesive Modified by Epoxy Resin in Laminated Films;
环氧改性水性聚氨酯胶粘剂在复合薄膜中的应用
2.
It was found that the properties of copolymer PUA were super to that blend PUA in the applications of laminated films.
结果表明,在复合薄膜应用方面,共聚型PUA乳液的性能优于共混型PUA乳液。
3.
A series of aqueous polyurethane adhesives were synthesized by means of four polymer polyatomic alcohols;properties of aqueous polyurethane adhesives were investigated taking vacuum aluminum laminated films of VMCPP, VMPET,OPP,and PE as laminated films;at the same time,the effect of polyurethane structure on peeling strength and drying speed of isocyanates and adding solvent were analyzed.
用不同结构聚酯二元醇为原料合成出一系列水性聚氨酯(PU)胶粘剂,以CPP镀铝膜、PET镀铝膜、OPP、PE为复合薄膜,探讨了聚酯结构对水性PU胶粘剂粘接性能的影响,同时还分析了异氰酸酯类型、外加溶剂对剥离强度和干燥速度的影响。
6) Film laminated
薄膜复合
补充资料：复合薄膜
由两层或多层不同材料的薄膜复合而成的高分子材料，主要用于包装。通过复合，可以获得具有各单一材料综合性质的材料，使用的基材主要有塑料薄膜（如聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯和聚酯等）、玻璃纸、纸张和金属箔等。基材的复合可以采用挤出复合方法或借助于胶粘剂进行胶粘复合。
以聚乙烯为例。其挤出复合方法(图1)是将聚乙烯投入料斗，经过挤出机从细缝挤出一定厚度熔融膜，与送入的基材在压力滚筒和冷却滚筒之间复合、卷取，即得制品。从冷却滚筒引入第二基材，可制得聚乙烯夹心的三层复合膜；如在该复合膜两侧再复以聚乙烯，即可得五层复合膜。这种聚乙烯复合薄膜的用途相当广泛（见表）。
多层塑料复合薄膜也可采用共挤出方法(见挤出)制得。采用几台挤出机分别将几种不同的树脂引入一公共机头中，然后从口模中挤出，即得制品。
借助胶粘剂制取多层复合薄膜(图2)的装置是将胶粘剂用涂布机涂敷在薄膜或其他基材上，在干燥区干燥，然后与其他基材热压复合。基材涂敷胶粘剂后亦可先与其他基材复合，然后干燥。
以聚乙烯为例。其挤出复合方法(图1)是将聚乙烯投入料斗，经过挤出机从细缝挤出一定厚度熔融膜，与送入的基材在压力滚筒和冷却滚筒之间复合、卷取，即得制品。从冷却滚筒引入第二基材，可制得聚乙烯夹心的三层复合膜；如在该复合膜两侧再复以聚乙烯，即可得五层复合膜。这种聚乙烯复合薄膜的用途相当广泛（见表）。
多层塑料复合薄膜也可采用共挤出方法(见挤出)制得。采用几台挤出机分别将几种不同的树脂引入一公共机头中，然后从口模中挤出，即得制品。
借助胶粘剂制取多层复合薄膜(图2)的装置是将胶粘剂用涂布机涂敷在薄膜或其他基材上，在干燥区干燥，然后与其他基材热压复合。基材涂敷胶粘剂后亦可先与其他基材复合，然后干燥。