1) pre-oriented yarn
预取向丝
1.
The three-color Wulong PET filament of 385 dtex/120 f was prepared from normal PET pre-oriented yarn (POY), cation dyeable PET POY and black PET POY.
以常规涤纶预取向丝(POY)、阳离子染料可染涤纶POY、黑色涤纶POY为原料,生产385 dtex/120 f涤纶三舞龙丝,探讨了其假捻变形的生产工艺。
2.
The trial-production of 35 dtex/24 f fine denier polyester pre-oriented yarn with existing production equipment was introduced.
在公司现有的生产设备上试生产35dtex/24f细旦涤纶预取向丝(POY),研究了聚酯切片含水率、熔体温度、冷却吹风风速、卷绕速度等工艺条件对POY物理性能和条干不匀率的影响。
3.
The structure and mechanical properties of PA6 pre-oriented yarn (POY) and draw textured yarn (DTY) were measured and analyzed.
对PA6预取向丝(POY)和弹力丝(DTY)的结构、力学性能等进行测试分析,探讨了PA6 POY在DTY加工过程中结构的变化对染色性能的影响。
2) preoriented yarn
预取向丝
3) POY
预取向丝
1.
Discussion on Production Process of 120dtex/144f PET POY by Direct Spinning;
120dtex/144f涤纶直纺预取向丝生产工艺探讨
2.
Structural Performance of PTT POY and its Post-processing;
PTT预取向丝的结构性能及其后加工
3.
PROCESS TEST OF 82DTEX/68F POY;
82dtex／68f预取向丝的工艺调试
4) partially oriented yarn
预取向丝
5) PTT POY
PTT预取向丝
1.
According to the properties of PTT, the spinning process of PTT POY and its afterprocessing technology are summarized.
结合聚对苯二甲酸丙二醇酯(PTT)的特性,综述了PTT预取向丝的生产工艺及其后加工技术。
6) yarn eveness
预取向丝条干
补充资料：预取向丝
分子式：
CAS号：
性质：由高速熔体纺丝法得到部分取向的卷绕丝。纺丝速度为3000～3500m/min。纤维双折射率0.025～0.060。断裂伸长150%～100%。结晶度<5%。结构稳定。存放、运输过程不变质。后加工性良好。采用高速纺丝成形，丝条受高张力作用使大分子沿纤维轴方向发生部分取向，便得到预取向丝。主要用于加工变形丝(DTY，TY)和拉伸丝(DY)。
CAS号：
性质：由高速熔体纺丝法得到部分取向的卷绕丝。纺丝速度为3000～3500m/min。纤维双折射率0.025～0.060。断裂伸长150%～100%。结晶度<5%。结构稳定。存放、运输过程不变质。后加工性良好。采用高速纺丝成形，丝条受高张力作用使大分子沿纤维轴方向发生部分取向，便得到预取向丝。主要用于加工变形丝(DTY，TY)和拉伸丝(DY)。