The curing kinetics of epoxy-dicyclopentadiene bisphenol cyanate ester(DCPDCE)resin co-poly mer system was studied by'Ozawa'and'Kissinger'methods,and the activation energy,pre-exponential factor,as well as rate constant at different temperatures and total reaction order of the co-polymer were calculated.
采用Ozawa方法和Kissinger方法研究了环氧树脂和双环戊二烯双酚型氰酸酯树脂(DCPDCE)共聚体系的固化动力学,并计算了活化能、指前因子、不同温度下的反应速率常数和共聚物的总反应级数。
2) dicyclopentandiene bisphenol cyanate ester
双环戊二烯型氰酸酯树脂
1.
Cure reactions in the blend of dicyclopentandiene bisphenol cyanate ester with epoxy resin;
环氧树脂改性双环戊二烯型氰酸酯树脂固化反应性
3) Dicyclopentadienylbisphenol cyanate ester
聚双环戊二烯双酚氰酸酯
4) DCPD-containing phenolic resin
双环戊二烯酚树脂
1.
Using phenol and dicyclopentadiene(DCPD) as raw materials,a DCPD-containing phenolic resin(DPR) was prepared via Friedel-Crafts alkylation and a DCPD-containing epoxy resin(DER) was prepared via epoxidation of DPR with epichlorohydrin.
以苯酚和双环戊二烯为原料,通过Friedel-Crafts反应,合成了双环戊二烯酚树脂(DPR)。
5) bisphenol A dicyanate esters
双酚A型氰酸酯树脂(BADCy)
6) bisphenol A epoxy acrylate resin
双酚A环氧丙烯酸酯树脂
补充资料：双酚A
工业上双酚A系由苯酚和丙酮在酸性介质中缩合制得： 为了使反应完全，丙酮应略过量；当以硫酸为催化剂时，酸浓度为72.5％～73％，反应温度约40℃，反应在搅拌釜中进行。可以连续或间歇生产。产物经中和，真空转鼓过滤,离心分离,即得粗双酚A。为了满足聚合要求,粗双酚A需进一步精制，一般采用二甲苯-水萃取法。
用硫酸为催化剂，副反应多，粗双酚A即使经二甲苯-水萃取精制后,质量仍不能达到生产聚碳酸酯的要求，只能满足生产环氧树脂的需要，故工业上已使用干燥氯化氢为催化剂（以甲硫醇为助催化剂）。
用硫酸为催化剂，副反应多，粗双酚A即使经二甲苯-水萃取精制后,质量仍不能达到生产聚碳酸酯的要求，只能满足生产环氧树脂的需要，故工业上已使用干燥氯化氢为催化剂（以甲硫醇为助催化剂）。