1) ultramicro 4A zeolite
超微4A沸石
2) submicron 4A zeolite
亚微米级4A沸石
1.
By adding a small amount of NaCl to increase alkalinity and changing temperatures in hydrothermal system,submicron 4A zeolite was synthesized.
实验结果表明,在4A沸石合成体系中加入适量NaC l的同时,通过增加碱度、改变晶化温度,可以合成出亚微米级4A沸石。
3) submicron 4A-zeolite
亚微米4A沸石
1.
The synthesis of submicron 4A-zeolite as detergent assistant from water glass and bauxite in hydrothermal system with crystallization director were introduced, and the effects of various factors were investigated.
介绍了以水玻璃、铝矾土和晶化导向剂为原料合成洗涤助剂用亚微米4A沸石的工艺过程,考察了各因素对合成的影响,并对亚微米4A沸石的结构和性能进行了研究。
4) zeolite 4A
4A沸石
1.
Study on the synthesis of zeolite 4A and geopolymer and ion-exchange;
4A沸石和地质聚合物的合成与离子交换性能的研究
2.
New development of additive of non-phosphorous detergent-zeolite 4A;
无磷洗涤剂助剂4A沸石的新进展
3.
Influences of inorganic salt on crystallization of zeolite 4A;
无机盐对4A沸石晶化过程的影响
5) 4A Zeolite
4A沸石
1.
Synthesis of 4A Zeolite from Coal-series Kaolin;
煤系高岭土酸处理法合成4A沸石
2.
Influence of mixture system of SDS and CTAB on synthesis of 4A zeolite;
SDS与CTAB混合表面活性剂体系对合成4A沸石的影响
3.
Research of growth of 4A zeolite crystal for detergent;
洗涤剂用4A沸石晶体生长过程的研究
补充资料：4A沸石
分子式：
CAS号：
性质：又称Na12[(A1O2)12、(SiO2)12]27H2O 又称4A分子筛。白色固体颗粒。呈网络状结构，内含均匀小孔，孔径0.42nm，比表面积约为600m2/R，不溶于水和有机溶剂，能溶解于强碱和强酸。加热超过800℃时，重新结晶形成白硅石状的结构。有吸附水分，液体、气体及不饱和的有机物质。对钙离子有交换能力，理论交换能力为352CaCO3mg/g，一般为290～320mgCaCO3/g，白度≥95%，pH值10～11.5，表观密度0.3～0.5g/cm3，平均粒径为2μm，粒度分布≤4μm占85%以上。用作无磷洗涤剂的助剂，代替三聚磷酸钠；在石油和其他工业用作气体和液体的干燥、脱水净化等，也用作催化剂和软水剂。
CAS号：
性质：又称Na12[(A1O2)12、(SiO2)12]27H2O 又称4A分子筛。白色固体颗粒。呈网络状结构，内含均匀小孔，孔径0.42nm，比表面积约为600m2/R，不溶于水和有机溶剂，能溶解于强碱和强酸。加热超过800℃时，重新结晶形成白硅石状的结构。有吸附水分，液体、气体及不饱和的有机物质。对钙离子有交换能力，理论交换能力为352CaCO3mg/g，一般为290～320mgCaCO3/g，白度≥95%，pH值10～11.5，表观密度0.3～0.5g/cm3，平均粒径为2μm，粒度分布≤4μm占85%以上。用作无磷洗涤剂的助剂，代替三聚磷酸钠；在石油和其他工业用作气体和液体的干燥、脱水净化等，也用作催化剂和软水剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。