1) melting time
熔化时间
1.
The results indicated that melting temperature was the lowest and melting time was the shortest at basicity 1.
18时,粘结相的熔化温度最低,熔化时间最短;添加1。
2.
The results indicated that melting temperature is the lowest with melting time the shortest if nCaO∶nFe2O3=1∶1,and the phase s melting temperature/time increases.
结果表明,nCaO∶nFe2O3=1∶1时,粘结相的熔化温度最低,熔化时间最短;添加MgO粘结相的熔化温度升高,熔化时间变长;当w(SiO2)或w(Al2O3)为3%时,粘结相的熔化温度最低,熔化最快。
3.
By changing n_(Cao):n_(Fe_2O_3),MgO,SiO_2 and Al_2O_3 percentage,the fluidity and melting time of binding phase were discussed.
以高碱度烧结矿中的铁酸钙粘结相为研究对象,考察了粘结相的流动性和液相生成能力;实验研究了不同n_(C_aO):n_(Fe_2O_3)以及不同氧化镁、二氧化硅和三氧化二铝的铁酸钙粘结相的流动特性和熔化时间。
2) pre-arcing time
熔化时间(熔断器的)
3) Reflowing Time
软熔时间
5) Bridgewire
熔断时间
1.
Factors Influencing Fusing Time of Electric Initiator s Bridgewire;
电起爆器桥丝熔断时间影响因素分析
6) melting range
熔化区间
1.
The melting temperature and melting range of converter slag bearing vanadium and titanium oxides were measured.
研究了主要组元对含 V2 O5、Ti O2 钢渣熔化性温度及熔化区间的影响 ,提出了含 V2 O5、Ti O2 钢渣进行溅渣护炉的控制方向。
2.
Compared with conventional specimens,the molten temperature of the rapid solidification specimens can be reduced with smaller melting range.
与相同成分普通凝固试样相比,快速凝固试样的熔化温度降低,熔化区间变窄,熔化区间最大的减小幅度可达12。