1) contact angle
接触角
1.
Influences of surface tension of acid solution and contact angle of rock on the cleanup efficiency of surfactant;
表面张力和接触角对酸液助排率的影响研究
2.
Comparison of hypsometry and goniometry in contact angle measurement;
接触角测量的量高法和量角法的比较
3.
Surface free energy of basalt and glass fibers by contact angle method;
接触角法测玄武岩及玻璃纤维表面能实验
2) contact angles
接触角
1.
Through experimentation,the contact angles with pure water of 9 coal seam in Jinggezhuang Mining and 9 coal seam in Tangshan Mining were measured respectively.
通过试验,分别测定了开滦集团荆各庄矿9煤层、唐山矿9煤层煤样与纯水的接触角,再根据所选表面活性剂不同浓度的溶液和接触角的关系,得到使接触角为0°的最低浓度。
2.
In this study, the contact angles of four different reference liquids (distilled water, diiodomethane, formadide and glycerol) formed on the surfaces of wood treated with chromated copper arsenate(CCA) and other two new-emerging copper-based water-borne systems (commercial name: NW and NS) were measured with a sessile drop method.
该研究中测定了蒸馏水、二碘甲烷、甲酰胺和甘油等4种参照液体在不同水基防腐处理(包括铬化砷酸铜CCA以及另外两种商品名为NW和NS的处理)后的木材表面所形成的接触角,并根据酸碱作用理论计算得到其表面自由能及其两个分量———LifshizvanderWaals(LW)分量和酸碱作用(AB)分量。
3.
The surface structure and hydrophilicity on the surface of PTFE films were investigated by contact angles, XPS and SEM.
研究了不同反应条件对PTFE表面湿润性的影响;通过测定样品膜对水的接触角θ(投影法)。
3) angle of contact
接触角
1.
The results of ESCA showed poly(siloxane) moved to and was rich on the surface of the blend,making the angle of contact big,being hydrophobic.
接触角和ESCA测定结果表明 :聚硅氧烷向共混物表面迁移 ,富集在共混物表面 ,使其接触角增大 ,具有憎水性。
2.
Because the angle of contact on the surface layer at the top of the capillary tube is larger than zero degree,this induces diminution of the surface area and the surface tension,it also decreases the actual height of the liquid in the capillary tube.
指出,由于毛细管顶部表面层接触角大于零导致表面层面积减小、表面层张力减小,致使毛细管内液体实际上升高度减小,故而此第一类永动机的设计是不可能实现的。
4) water contact angle
接触角
1.
The results show that FPA-R has excellent hydrophobic and oleophobic property and low surface free energy, and the water contact angle of FPA-R film increases with th.
通过接触角的测定,研究了FMA用量和热处理对FPA-R胶膜疏水性和疏油性以及表面自由能的影响规律,同时研究了FPA-R共混改性PU涂饰剂涂膜的疏水性。
2.
The effect of the amount of organfluorine on the rate of water absorption as well as water contact angle of latex film was also studied.
通过热分解引发体系,用有机氟单体对丙烯酸树脂进行改性,合成了性能优异的氟改性丙烯酸乳液,并研究了有机氟单体对乳胶膜吸水率及对水的接触角的影响。
3.
In this case the water contact angle approaches zero and flow down when the surface leans.
如果玻璃非常平整及非常干净,水滴在玻璃上将自由展开,接触角为零。
6) contact angle
接触角法
1.
The compatibility、thermal stability and hydrophilicity of PVA/PA-6 alloy were studied by relative viscosity、refraction index、DSC、FTIR、TG and the contact angle.
采用黏度法、折光指数法、DSC法、FTIR法、TG法和接触角法研究了PVA/PA-6的相容性、热稳定性及亲水性。
2.
Several surface analysis technic and its application fields were introduced,such as contact angle(CA), ATR/FT-IR,XPS and so on.
综述了接触角法(CA)、衰减全反射/傅里叶变换红外光谱法(ATR/FT-IR)、X射线光电子能谱法(XPS)等几种表面分析技术的特点和应用领域,结合聚氨酯(PU)衬层的特点,提出了适用于表征PU衬层表面特性的一些方法。
补充资料：接触角
在固、液、气三相交界处,自固-液界面经过液体内部到气- 液界面之间的夹角称为接触角，通常以θ 表示(见图)。将一滴液体，放在一均匀平滑的固体表面上，一种情况是液体完全展开覆盖固体表面，另一种情况是液滴与固体表面形成一定角度停留于表面上。 液体在固体表面上的接触角与固-气界面自由能γSG、固-液界面自由能γSL及液体的表面张力γLG之间的关系，服从杨氏润湿方程：
γSG-γSL＝γLGcosθ此方程可看作在固、液、气三相交界处，三个界面张力之间平衡的结果。接触角的大小，可以反映液体对固体表面的润湿情况，接触角愈小，润湿得愈好。
通过测定接触角和液体的表面张力，利用杨氏润湿方程，可以得到粘附功、粘附张力、铺展系数的值，并能对各种润湿过程能否自动进行作出判断（见铺展）。
接触角的测定方法大体分为三类:①角度测量法,观测液滴或气泡在固体表面上的外形，并在固、液、气三相交点处作切线，用量角器直接量角度；②长度测量法，通过对在固体表面上液滴的高度、宽度等的测量，计算出接触角,如液滴最大高度法、吊片法等；③重量法,利用吊片法测定液体表面张力的原理，可以测定液体对固体（吊片）的接触角。
在测量接触角时，若在固－液界面扩展后测量，此接触角称前进角，通常以θA表示；若在固－液界面缩小后测量，此接触角为后退角，用θR表示。通常前进角与后退角的数值不等,两者之差值(θA-θR)叫做接触角滞后。造成接触角滞后现象的主要原因是液体或固体表面被污染，固体表面的粗糙不平和不均匀性，以及某些高聚物表面上大分子链段的流动性。表面的不平不仅影响接触角滞后，而且还影响接触角数值。粗糙度对接触角的影响可用温策尔方程表示：
γ＝cosθ′/cosθ式中γ为粗糙因子,是表面粗糙化后的真实表面积与表观表面积之比。θ′为在粗糙化表面上的接触角。θ为在平滑表面上的接触角。当θ＜90°时,表面愈粗糙，θ′值愈小；而当θ＞90°时，表面粗糙化使θ′变大。
γSG-γSL＝γLGcosθ此方程可看作在固、液、气三相交界处，三个界面张力之间平衡的结果。接触角的大小，可以反映液体对固体表面的润湿情况，接触角愈小，润湿得愈好。
通过测定接触角和液体的表面张力，利用杨氏润湿方程，可以得到粘附功、粘附张力、铺展系数的值，并能对各种润湿过程能否自动进行作出判断（见铺展）。
接触角的测定方法大体分为三类:①角度测量法,观测液滴或气泡在固体表面上的外形，并在固、液、气三相交点处作切线，用量角器直接量角度；②长度测量法，通过对在固体表面上液滴的高度、宽度等的测量，计算出接触角,如液滴最大高度法、吊片法等；③重量法,利用吊片法测定液体表面张力的原理，可以测定液体对固体（吊片）的接触角。
在测量接触角时，若在固－液界面扩展后测量，此接触角称前进角，通常以θA表示；若在固－液界面缩小后测量，此接触角为后退角，用θR表示。通常前进角与后退角的数值不等,两者之差值(θA-θR)叫做接触角滞后。造成接触角滞后现象的主要原因是液体或固体表面被污染，固体表面的粗糙不平和不均匀性，以及某些高聚物表面上大分子链段的流动性。表面的不平不仅影响接触角滞后，而且还影响接触角数值。粗糙度对接触角的影响可用温策尔方程表示：
γ＝cosθ′/cosθ式中γ为粗糙因子,是表面粗糙化后的真实表面积与表观表面积之比。θ′为在粗糙化表面上的接触角。θ为在平滑表面上的接触角。当θ＜90°时,表面愈粗糙，θ′值愈小；而当θ＞90°时，表面粗糙化使θ′变大。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。