1) sintering mullite
烧结莫来石
2) Zirconium Mullite
烧结锆莫来石砖
1.
With different structures to electromelt-ing brick, Zirconium Mullite Sintered Brick which used as backwall of float glass furnace are agglutinated by mullite and zircon.
玻璃熔窑前脸墙用烧结锆莫来石砖,是由莫来石作为骨科和锆英石烧结而成的,它的结构与电熔砖有明显的区别,通过观察烧结锆莫来石砖使用前后的结构变化,了解其蚀变过程,从而了解烧结锆莫来石砖可能形成的玻璃结石形态。
4) Mullite bonded
莫来石结合
5) mullite
['mʌlait]
莫来石
1.
Effect of Mullite on Property of Aluminium Titanate;
莫来石对钛酸铝陶瓷组织性能的影响
2.
Research on thermal shock resistance of alumina-aluminium titanate-mullite ceramics;
氧化铝-钛酸铝-莫来石复相陶瓷抗热震性研究
3.
The influence of sintering technique on crystalline phases and microstructures of mullite synthesized;
烧结工艺对合成莫来石晶相结构的影响
6) mullitization
莫来石化
1.
Effects of different types alumina powders and amount of active alumina added on andalusite decomposition,primary mullitization and secondary mullitization were studied by analyzing XRD data.
研究了几种氧化铝原料对红柱石基耐火材料莫来石化行为的影响。
2.
Temperature and soaking time on mullitization of andalusite were studied by analyzing the XRD data.
研究了烧成温度和保温时间对添加活性氧化铝的红柱石基耐火材料莫来石化行为的影响。
3.
The current status and progress in the preparation of mullite precursor powders by chemicalmethods and the mullitization mechanism at low temperatures are reviewed.
对化学法制备莫来石粉料的研究现状进行了系统的总结,阐述了低温莫来石化的机理。
补充资料：莫来石陶瓷低温烧结
一种莫来石陶瓷低温烧结方法，属陶瓷低温烧结方法，该方法的特点是先将硝酸铝与正硅酸乙酯的乙醇溶液混合制成莫来石单相凝胶，该凝胶干燥后可在980～1000℃烧结转化成莫来石。将该凝胶加入到烧制莫来石陶瓷的原料中，由于是液体，因此能得到均匀混合。烧结过程中，莫来石单相凝胶在现转化为莫来石，类似于晶种一样均匀分布在莫来石陶瓷原料中，促进烧结，可在1400℃完成烧结，比传统方法降低200℃，从而大大降低了能耗。
主权项
1.一种莫来石陶瓷低温烧结方法，其特征在于，包括下述顺序的步骤： (1)把正硅酸乙酯与硝酸铝的乙醇溶液混合，密封后室温放置2～4天，获得莫来石单相溶胶，其中硝酸铝与正硅酸乙酯的摩尔比为3∶1，该莫来石单相溶胶干燥后可在980～1000℃之间转化为莫来石陶瓷； (2)取莫来石单相凝胶适量作为添加剂，添加到烧制莫来石陶瓷的原料中，搅拌均匀，所加入的莫来石单相凝胶中氧化铝加上氧化硅的重量为陶瓷原料总重的2～5％； (3)上述莫来石原料烧结，在1200～1300℃保温0.5～2小时，在1400℃保温 1～3小时。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。