1) 20CrMnTiH gear steel
20CrMnTiH齿轮钢
1.
Present situation and quality control of 20CrMnTiH gear steel in Laiwu Steel;
莱钢20CrMnTiH齿轮钢的质量现状与质量控制
2.
Practice of Process for Increasing Ratio of Qualified 20CrMnTiH Gear Steel Products with Non-metallic Inclusion Examination
提高20CrMnTiH齿轮钢夹杂物合格率的工艺实践
3.
Starting with the requirements in serviceability and malleability which must be met during the machining of gears,based on the present situation of 20CrMnTiH gear steel in the Special Steel Plant,this paper presents the main points in quality control of the steel during its production and puts forth some improvement suggestions.
主要从齿轮加工时必须满足的使用性要求和加工性要求两个方面着手,结合特钢厂20CrMnTiH齿轮钢的质量现状,介绍了该钢种生产时的质量控制要点,并提出改进建议。
2) Gear Steel 20CrMnTiH
20CrMnTiH齿轮钢
1.
Process Practice of Gear Steel 20CrMnTiH Production by 150 mm×150 mm Concasting Billet at Laiwu Steel;
莱钢150mm×150mm连铸坯生产20CrMnTiH齿轮钢的工艺实践
2.
Process Practice of Gear Steel 20CrMnTiH Production with 70 t LD-LF-CC Flow Sheet at Chengde Jianlong Steel
承德建龙70tLD-LF-CC流程生产20CrMnTiH齿轮钢的工艺实践
3.
Pilot Production of Narrow Hardenability Band Gear Steel 20CrMnTiH by 120 t Converter-LF+RH Process at Panzhihua Steel;
攀钢采用120 t转炉-130 t LF+RH-280 mm×380 mm方坯连铸-热轧工艺生产Φ25～160 mm 20CrMnTiH齿轮钢(%:0。
3) 20CrMnTiH Steel
20crMnTiH钢
1.
Critical strain model of 20CrMnTiH steel
20CrMnTiH钢临界应变模型研究
2.
Based on an analysis of fractures of 20CrMnTiH steel samples with pinholes and the content of nitrogen,oxygen and hydrogen and a combination of means like metallographic examination and SEM,it is thought that the main cause for pinhole defects in macro samples is high hydrogen content in steel.
对20CrMnTiH钢低倍检验中存在针孔的试样进行断口和氮、氧、氢含量分析,并结合金相和电镜分析等手段,认为低倍试样上针孔状缺陷的主要原因是钢中氢含量高形成的气孔。
4) Gear Steel
齿轮钢
1.
Multi-Field Coupled Analysis on Quenching Process of Gear Steel;
齿轮钢淬火过程多场耦合分析
2.
Effect of deformation of austenite on continuous cooling transformation for 22CrSH gear steel;
奥氏体变形对22CrSH齿轮钢连续冷却相变的影响
3.
The Development of the High Grade Gear Steel SCM420H;
高等级齿轮钢SCM420H的开发研制
5) Gear Steel 28MnCr5
28MnCr5齿轮钢
1.
Effect of LF(VD) Refining Process on Control of Sulphur and Sulphide in Gear Steel 28MnCr5;
LF(VD)精炼工艺对控制28MnCr5齿轮钢中硫和硫化物的影响
6) Gear Steel 20CrMnTiH1
20CrMnTiH1齿轮钢